Abstract:Tungsten and water co-doped indium oxide (IWOH) films were deposited via a low-damage reactive plasma deposition method at room temperature followed by air atmosphere annealing. The structural, electrical, and optical properties of IWOH films with different water flow rates (FH2O) were systematically investigated before and after annealing. Despite the lower mobility (43.7 cm2/V) of IWOH films with high water flow rate (H-FH2O, FH2O ≥ 1.5 sccm) in the as-deposited state, it has increased to 65.2 cm2/V, which surpassed IWOH films with low water flow rate (L-FH2O, FH2O < 1.5 sccm) after annealing. Meanwhile, a significant increase in average optical transmittance from 80.9% to 88.8% and from 92.2% to 95.2% in the short wavelength of visible (350–500 nm) and near-infrared region (800–2500 nm), respectively, was obtained for H-FH2O films after annealing. The variation of the optical and electrical properties for IWOH films with different FH2O was attributed to the crystalline structure with a larger crystallite size and lower density of grain boundary. X-ray diffraction, scanning electron microscopy, and X-ray photoelectron spectroscopy analysis revealed that high water flow rate impeded crystallization of IWOH films during reactive plasma deposition, leading to an amorphous structure in the as-deposited state. After annealing, however, the H-FH2O films crystallized and exhibited larger grains than both tungsten-doped indium oxide (IWO) and L-FH2O films. The modified crystalline properties of IWOH films with larger grains hence reducing grain-boundary scattering, which was realized by H-FH2O and annealing treatment, gave rise to enhanced electrical properties without deteriorating optical properties.

Water-Immersion Laser-Scanning Annealing for Improving Polycrystalline Au Films

High-Pressure Water-Vapor Annealing for Enhancement of A-Si:H Film Passivation of Silicon Surface

Influence of Post-Annealing Treatment on the Morphology of Au Films Deposited on Liquid Surfaces

Influence of annealing on microstructure and electrochromic properties of WO3 thin film

In Situ Optical Characterizations of the Annealing Effects Upon Sno2: F Films by Spectroscopic Ellipsometry

Crystallization and Disappearance of Defects of the Annealed Silicon Nanowires

Optimization of Material Structure of Ploy-Si Thin Film Based on Al Induced Crystallization

Influence of annealing on microstructures and photoluminescence of nano-composite silicon film

Crystallization of Hydrogenated Amorphous Silicon Thin Films Using Combined Continuous Wave Laser and Thermal Annealing

Low-Temperature Annealing Induced Amorphization in Nanocrystalline NiW Alloy Films

Annealing treatment on waterborne polyurethane film-forming and structural features induced heat conduction performance in conductive adhesive

Imaging Scatterometer for Observing In-Situ Changes to Optical Coatings During Air Annealing

Effect of Annealing on SiC Thin Films Prepared by Pulsed Laser Deposition

Annealing Behavior and Hardness Enhancement of Amorphous Sicn Thin Films

The Annealing Effect of Crystal 4H-Sic Films Prepared by Pulsed Laser Deposition

Annealing behaviors of structural, interfacial and optical properties of HfO 2 thin films prepared by plasma assisted reactive pulsed laser deposition

Thermal Stability Improvement Induced by Laser Annealing for 50-Å Ni(Pt) Film Silicidation

Effect of crystalline structure on optical and electrical properties of IWOH films fabricated by low-damage reactive plasma deposition at room temperature

Influence of Annealing Condition on Crystallization Behavior and Mechanical Properties of Thermal Sprayed PEEK Coating

Effect of Laser Scanning Speed on Microstructure of Electroplated Copper Films During Laser Scanning Annealing

Effect of Annealing on the Structural, Magnetic, Surface Energy and Optical Properties of Co32Fe30W38 Films Deposited by Direct-Current Magnetron Sputtering