Abstract:In this study, crack-free composite coatings with ratios of 40%, 50%, and 60% WC10%-Ni60AA cermet/Inconel 718 were successfully prepared using laser directed energy deposition. WC10%-Ni60AA cermet, as a reinforced particle, consists of 10% tungsten carbide (WC) particles and 90% nickel-based alloy. The bottom layers of the composite coatings were metallurgically well-bonded with substrates. The microstructures of the middle and top layers exhibited a novel eutectic precipitate skeleton structure (Cr23C6 phase), accompanied by an embedded nano-precipitate (MC (M: Nb, Mo) phase). The proportion of the eutectic precipitate skeleton structure increased with an increase in cermet content; in particular, the 60% cermet/Inconel 718 coating exhibited the largest proportion of the skeleton structure, with an area density of 86.15%. An increase in the cermet content improved the grain refinement in the composite coating. Fine equiaxed crystals were obtained in the 60% cermet/Inconel 718 coating, in which the proportion of high-angle grain boundaries (>15°) was 85.7% and the average grain size was 35.77 μm. Furthermore, the hardness and wear resistance of the composite coatings improved as the cermet content increased. The average hardness of the 60% cermet/Inconel 718 coating was 503 HV0.1 and wear loss was 107.9 mg, thereby exhibiting the best wear resistance owing to the synergistic effects of precipitation strengthening, grain refinement strengthening, and dispersion strengthening (unmelted and retained WC particle). Adhesive and abrasive wear were dominant wear mechanisms in the 40% cermet/Inconel 718 coating, whereas oxidative wear and abrasive wear were dominant in the 50% and 60% cermet/Inconel 718 coatings.

Adhesive wear performance of hardmetals and cermets

Research On Wear Behavior Of Atc Cermet Material

Friction and dry sliding wear behaviour of cermets

Adhesive and abrasive wear behaviour of TiC alloyed, sintered, austenitic stainless steels

A Comparative Study on the Wear Performance and High-Temperature Oxidation of Co-Free Cermets and Hardmetals

Effect of abrasive particle size and the influence of microstructure on the wear mechanisms in wear-resistant materials

Sliding wear behavior of cold metal transfer cladded Stellite 12 hardfacings on martensitic stainless steel

The Dry Sliding Wear Behavior of HVOF-Sprayed WC: Metal Composite Coatings

Abrasive and adhesive wear behaviour of metallic bonds in a synthetic slurry test for wear prediction in reinforced concrete

Effect of tungsten carbide content on the tribological behavior of TiB2–TiC-based cermets

Defect initiation and accumulation kinetics in hard-coated WC-Co hardmetal under multi-axial loads at elevated temperature in a novel ball-in-cone test setup

Reciprocating Wear Performance and Interfacial Microstructure of a TiC–Ni 2 AlTi Cermet

Microstructure, mechanical and friction-wear properties of SiC-WC composite with Al and C as sintering aids

Tribological characteristics of WC-Cr3C2-Ni cermet coatings under different wear parameters

Microstructural evolution and wear resistance of composite WC10%-Ni60AA cermet built by laser directed energy deposition

First-principles simulations of metal-ceramic interface adhesion: Co/WC versus Co/TiC

Effect of Percentage Variation on Wear Behaviour of Tungsten Carbide and Cobalt Reinforced Al7075 Matrix Composites Synthesized by Melt Stirring Method

Preparation, mechanical properties and wear resistance of dual-sized TiC particles reinforced high-entropy alloy cermet coating

Study on the friction and wear properties of nickel-based-WC-10Ni composite coatings prepared on the surface of TC4 titanium alloy

Enhanced Adherence, Brittleness, Corrosion, and Sliding Wear by Adding NiCrFeBSiC-Mo on WC-Co Coatings and Hardened Substrates

ASSESSMENT OF WEAR AND DESTRUCTION OF SOLID CARBIDE CUTTERS DURING MILLING OF HARDENED STEEL 4X5MF1C WITH A HARDNESS OF 52 HRC