Abstract:This work studies the effect of mechanical properties and microstructure on sliding wear and cavitation erosion behaviors of cermet coatings deposited via high velocity oxy-fuel (HVOF) spraying on AZ31 magnesium substrate. Cavitation tests indicated that WC-Co-Cr cermet had superior resistance to cavitation erosion than WC-Cr 3 C 2 -Ni, WC-Co coatings, and far better resistance than the AZ31 expressed by the volume material loss 3.74 mm 3 , 6.99 mm 3 , 10.30 mm 3 , and 108.82 mm 3 , respectively. WC-Co-Cr coating's erosion mechanism exhibited uniform material removal, which slows the erosion rate. The CoCr binder prevented severe surface pitting and the detachment of the WC-Co-Cr cermet material in massive chunks which was observed for WC-Co and WC-Cr 3 C 2 -Ni coatings. Cermet coatings microstructure discontinuities such as pores and ceramic-metallic phase interfaces are the centers of material erosion. No clear correlation between the erosion behavior and mechanical properties of coatings was revealed. Contrary to that, sliding wear results were strongly related to the mechanical properties. The WC-Co-Cr and WC-Co samples exhibited higher hardness and higher values of Young's modulus than the WC-Cr 3 C 2 -Ni one. The generated stresses with lower values of hardness and Young's modulus for the WC-Cr 3 C 2 -Ni sample resulted in a higher wear factor, approx. 1·10 −7 mm 3 ·N −1 ·m −1 . For the harder samples, which exhibited higher stiffness (WC-Co-Cr and WC-Co), this type of wear resulted in lower values of the wear factor: 6·10 −8 mm 3 ·N −1 ·m −1 and 9·10 −8 mm 3 ·N −1 ·m −1 , respectively. Deposition of the cermet coatings effectively protected the magnesium substrate, which shows low resistance to cavitation erosion and sliding wear when uncoated.

Tribological characteristics of WC-Cr3C2-Ni cermet coatings under different wear parameters

Research On Wear Behavior Of Atc Cermet Material

The Dry Sliding Wear Behavior of HVOF-Sprayed WC: Metal Composite Coatings

Three-Body Abrasive Wear Behavior of WC-10Cr3C2-12Ni Coating for Ball Mill Liner Application

Study on the friction and wear properties of nickel-based-WC-10Ni composite coatings prepared on the surface of TC4 titanium alloy

Sliding friction behaviors of TiCN/Cr 3 C 2 -NiCr and TiCN/WC-CoCr duplex coatings fabricated by combining HVOF and HT-CVD procedures

Microstructure and wear behaviors of a WC10%-Ni60AA cermet coating synthesized by laser-directed energy deposition

Impact-sliding wear properties of PVD CrN and WC/C coatings

Friction and wear behavior of Ni-based alloy coatings with different amount of WC–TiC ceramic particles

Enhanced Fracture Toughness of WC-CoCr Thermally Sprayed Coatings by the Addition of NiCrFeSiBC and Mo and Its Influence on Sliding Wear Behavior

Microstructure and mechanical property of high velocity oxy-fuel sprayed multimodal WC-Cr3C2–Co–Y2O3 cermet coating

Friction and dry sliding wear behaviour of cermets

Investigations of cavitation erosion and wear resistance of cermet coatings manufactured by HVOF spraying

Reciprocating Wear Performance and Interfacial Microstructure of a TiC–Ni 2 AlTi Cermet

75Cr3C2-25NiCr and 86WC-10Co-4Cr High Wear- and Corrosion-Resistant Cermet Coatings Deposited on A356 Substrate by High-Velocity Oxy-Fuel Technique

Enhanced Adherence, Brittleness, Corrosion, and Sliding Wear by Adding NiCrFeBSiC-Mo on WC-Co Coatings and Hardened Substrates

Tribological Performance and Wear Mechanism of Laser Cladded NiCrAl-WC Coatings at High-Temperature

Tribological behavior of NiCrW-based self-lubricating composites against IC10 alloy under high temperature and extremely slow sliding speed

High-Temperature Wear Behavior and Mechanisms of Self-Healing NiCrAlY-Cr3C2-Ti2SnC Coating Prepared by Atmospheric Plasma Spraying

Comparative Study of Mechanical Performance of AlCrSiN Coating Deposited on WC-Co and cBN Hard Substrates