Abstract:In this study, the effect of TiCN and WC-Co coatings on the tribological performance of spheroidal graphite cast iron materials was investigated by wear tests under dry and lubricated conditions. The mechanical and physical effects of the coating processes were analysed by microhardness measurements and visual methods (SEM, EDX, XRD). The tribological effect of WC-Co and TiCN coated specimens were investigated by ball-on-plate wear tests carried out under dry and boron oil emulsion (5% concentration) conditions at 50 N load and 60 rpm sliding speed parameters. The friction coefficient and wear volume results were obtained to investigate the effect of the coating process and boron oil emulsion on friction and wear behaviour. The wear mechanisms were determined with SEM images obtained from the worn surfaces and surfaces analysed elementally with EDX images. Additionally, surface morphology was examined with surface roughness measurements and 2D–3D topography images. According to the microhardness measurement results, it was observed that the spheroidal graphite cast iron with 290 HV hardness reached 1559 HV with TiCN coating and 1440 HV with WC-Co coating. According to the wear test results, it was determined that TiCN and WC-Co coatings decreased the friction coefficient by 32.51% and 12.80%, respectively. When the effect of boron oil usage compared to dry environmental conditions, it was concluded that the friction coefficient and wear volume decreased by a maximum of 54.80% and 53.70%, respectively. Additionally, the roughness values decreased in the experiments where the boron oil emulsion was used. However, although the TiCN coating improved the surface quality, the WC coating negatively affected the surface quality. Surface form images obtained with 2D and 3D topography also support the alteration in roughness values.

Friction and dry sliding wear behaviour of cermets

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Research On Wear Behavior Of Atc Cermet Material

The Effects of Ageing and Whisker-Orientation on Wear Behaviour of SiCwAl Composites under Unlubricated Sliding Friction

Tribological characteristics of WC-Cr3C2-Ni cermet coatings under different wear parameters

Adhesive wear performance of hardmetals and cermets

Wear Behaviors of Ticn Cermet under Different Concentrations of Abrasive Slurries from Carborundum, Corundum and Silica Sands

Reciprocating Wear Performance and Interfacial Microstructure of a TiC–Ni 2 AlTi Cermet

Friction and wear behavior of Ti(C,N) self-lubricating cermet materials with multilayer core-shell microstructure

The Dry Sliding Wear Behavior of HVOF-Sprayed WC: Metal Composite Coatings

A Comparative Study on the Wear Performance and High-Temperature Oxidation of Co-Free Cermets and Hardmetals

Abrasive Wear Behavior of Ticn Cermets under Water-Based Slurries with Different Abrasives

Carburization And Wear Behavior Of Self-Lubricating Ti(C,N)-Based Cermets With Various Secondary Carbides

SEM and SEAM study on tribological performance of cermets coatings

Dry Sliding Behavior and Particulate Emissions of a SiC-graphite Composite Friction Material Paired with HVOF-Coated Counterface

Friction and wear of titanium alloys sliding against metal, polymer, and ceramic counterfaces

Investigation of wear behavior of carbide based coated rolling roll materials under dry and lubricated conditions

Study on the growth and wear characters of CVD coating deposited on Ti(C, N)-based cermets with adding different C/N ratios of Ti(C, N) powders

Effect of tungsten carbide content on the tribological behavior of TiB2–TiC-based cermets

Tribological Properties of Ti3SiC2 Coupled with Different Counterfaces

Sliding friction behaviors of TiCN/Cr 3 C 2 -NiCr and TiCN/WC-CoCr duplex coatings fabricated by combining HVOF and HT-CVD procedures