Reciprocating Wear Performance and Interfacial Microstructure of a TiC–Ni 2 AlTi Cermet

Hui Zhang,Xiaohui Wang,Mingyue Liu,Xuanming Fang

DOI: https://doi.org/10.1007/s11249-014-0348-6

2014-01-01

Tribology Letters

Abstract:Wear performance of a near equi-volume TiC–Ni 2 AlTi cermet with minor NiAl was evaluated by reciprocal sliding against Si 3 N 4 balls. Both coefficient of friction (COF) and specific wear rate (SWR) decrease with the applied load in the range from 5 to 20 N, reaching minimums of 0.34 and 2.2 × 10 −6 mm 3 /Nm, respectively, at 20 N. To understand the novel wear resistance, interfacial microstructure was investigated. As indicated by high resolution transmission electron microscopy observations, the interfaces are either coherent (TiC/NiAl and Ni 2 AlTi/NiAl) or semi-coherent (TiC/Ni 2 AlTi). Depending on the grain size of Ni 2 AlTi, two types of TiC/Ni 2 AlTi interface were observed. For the micrometer or sub-micrometer sized Ni 2 AlTi grains, the orientation relationship (OR) is (111) TiC ∥ (220) Ni 2 AlTi, [1 1̅ 0] TiC ∥ [1 1̅ 0] Ni 2 AlTi, while for the Ni 2 AlTi grains in tens of nanometers, the OR is (020) TiC ∥ (002) Ni 2 AlTi, [101] TiC ∥ [010] Ni 2 AlTi. The strongly bonded coherent and semi-coherent interfaces impede the failure of the heterophase boundaries, which accounts for the excellent wear resistance of the newly prepared cermet.