Improved wear resistance of TiAl composite coatings through NbC@(Ti,Nb) 2 AlC core-shell structure and nanoscale precipitation strengthening

Yuming Zhu,Xiaojie Song,Minglei Liu,Wenchang Jia,Zeliang Yin,Quanzhi Wang,Yuhao Zhang,Di Jiang,Qiang Song,Hongzhi Cui

DOI: https://doi.org/10.1016/j.vacuum.2023.112091

IF: 4

2023-04-26

Vacuum

Abstract:TiAl metal-based composite coatings are fabricated by laser cladding on Ti-6Al-4V (TC4) surfaces to improve their wear resistance and expand its application rang. In this study, the NbC ceramic phase and the Cu alloying element are added to improve the performance of TiAl composite coatings. The results show that the microstructure is mainly composed of TiAl, Ti 3 Al matrix phase, core-shell structure is NbC or TiC as the core and (Ti,Nb) 2 AlC as the shell, and the (Nb, Ti)Al 2 Cu 2 phase with increasing Cu content. The composite coating achieves a maximum hardness of 1048.8 HV 0.2 and a minimum wear rate of 9.5 × 10 −8 mm 2 /N, which respectively represents an increase of 3 times and 5.2 times compared with TC4. The wear mechanism is abrasive wear . The SEM and TEM analyses and the nanoindentation results show that the main reasons for the good friction properties are (i)the increased hardness; (ii)the good interfacial relationship of the core-shell structure; (iii) the presence of the (Nb,Ti)Cu 2 Al 2 phase reinforced by nanoscale precipitates. A detailed explanation of the wear mechanism of composite coatings, counterbody of morphology and a systematic explanation of the role of wear debris in the friction process through experimental design are provided in this paper.

materials science, multidisciplinary,physics, applied