Abstract:Ti-Al-C-Nb x ( x = 0, 2, 4, 6, and 8 at%) composite coatings are prepared on the surface of TC4 titanium alloy via laser cladding. The effect of Nb content on the microstructure, hardness and tribological properties of the Ti-Al-C-based coatings are investigated. The results show that the coatings are composed of Ti3Al, TiC, Ti2AlC, Ti2AlNb, and Ti3AlC2 phases. In the coating with an Nb content of 2 at%, a large amount of flocculent Ti3AlC2 phase precipitated. This is attributed to the solid solution of a small amount of Nb into the Ti3AlC2 phase, promoting the heterogeneous nucleation of Ti3AlC2. With the increase of the Nb content, more Nb atoms are incorporated into the Ti3AlC2 phase through solid solution, causing the decomposition of Ti3AlC2 into Ti2AlC and TiC. When the Nb content is 8 at%, the flocculent Ti3AlC2 phase almost completely disappeared. The Ti-Al-Nb matrix, hard TiC particles and Ti 3 AlC 2 MAX phase form a composite structure with synergistic effects. This enhanced the friction and wear reduction properties of the coatings and reduced the hardness difference between the matrix and the reinforcing phases.

Effect of Nb Content on the Tribological Properties of Laser-Cladded Ti-Al-C MAX Phase Composite Coatings