Effects of Ti/Nb Dual-Element Addition on the Microstructure and Properties of Tungsten Carbide-Reinforced Laser Cladding Coatings

Jianfeng Li,Xue Gao,Kewei Dong,Jinfu Liu

DOI: https://doi.org/10.3390/coatings14060708

IF: 3.236

2024-06-05

Coatings

Abstract:Metal-ceramic composite coatings are produced on the surface of equipment components by laser cladding, improving the abrasive wear resistance of components and extending their service life. However, defects such as brittleness and cracks limit the wide application of metal-ceramic clad coatings in the field of construction machinery. In the present study, a dual-element (Ti/Nb) alloying method is innovatively adopted to regulate the microstructure and mechanical properties of tungsten carbide (WC)-reinforced clad coatings. Experimental results show that with the introduction of Ti/Nb, novel reinforcements are in-situ synthesized in the cladding coatings with two different kinds of morphologies: one is a core-shell carbide with the core of pure TiC and a shell of (Ti,Nb,W)C multiple carbide; the other is a (Ti,Nb,W)C multiple carbide. With 8 wt.% Ti/Nb addition, the newly formed multiple carbides with the appropriate content are well-dispersed and distributed in the clad coating, which effectively transfers load, inhibits the initiation and expansion of micro-cracks, and resists the wear damage of hard abrasive particles, solving the technical problems of the simultaneous improvement of toughness and abrasive wear resistance of metal-ceramic laser cladding coatings.

materials science, multidisciplinary, coatings & films,physics, applied

What problem does this paper attempt to address?

The problem that this paper attempts to solve is in laser cladding technology, by adding a dual - element (Ti/Nb) alloying method to adjust the microstructure and mechanical properties of tungsten carbide (WC) - reinforced cladding coatings, thereby simultaneously improving their wear resistance and crack resistance. Specifically, the research aims to solve the following two main problems:

1. **Formation of brittle phase M23C6**: In the high - temperature molten pool, WC is easily dissolved, releasing free W and C elements. As the molten pool solidifies, due to the metallurgical chemical reactions between W, C and the alloy elements in the molten pool, the brittle M23C6 phase will be precipitated, which is an important reason for cracks in the cladding coating.

2. **Uneven distribution of WC particles**: Due to the relatively high density of WC particles (15.7 g/cm³), they are prone to sink in the molten pool, resulting in a gradual decrease in the WC content in the cladding coating from the bottom to the top, making the mechanical properties of the coating uneven along the depth direction.

To solve these problems, the author adopted a dual - element (Ti/Nb) alloying method and experimentally studied the effects of different Ti/Nb contents on the microstructure, crack sensitivity, and wear resistance of WC/Fe cladding coatings. The research shows that after adding Ti/Nb, two new strengthening phases with different morphologies are formed: one is a core - shell structure with a pure TiC core and a (Ti, Nb, W)C multi - carbide shell; the other is a non - nucleated (Ti, Nb, W)C multi - carbide. These newly formed multi - carbides can effectively disperse the load, inhibit the generation and propagation of micro - cracks, and resist the wear of hard abrasive particles, thus solving the technical problem of simultaneously improving the toughness and wear resistance of WC/Fe cladding coatings.