Lattice distortion in selective laser melting (SLM)-manufactured unstable β-type Ti-15Mo-5Zr-3Al alloy analyzed by high-precision X-ray diffractometry

Aya Takase,Takuya Ishimoto,Ryoya Suganuma,Takayoshi Nakano

DOI: https://doi.org/10.1016/j.scriptamat.2021.113953

IF: 6.302

2021-08-01

Scripta Materialia

Abstract:<p>A peculiar lattice distortion in a selective laser melting (SLM)-manufactured unstable β-type Ti-15Mo-5Zr-3Al was observed for the first time, through high-precision X-ray diffraction (XRD) analyses. After SLM, Ti-15Mo-5Zr-3Al exhibited a body-centered-tetragonal structure instead of a body-centered-cubic structure; the <em>c</em>-axis was 0.63% shorter than the <em>a</em>-axis. The XRD analyses also revealed tensile residual stresses of 210 ± 12 MPa at the specimen surface. A numerical simulation indicated rapid cooling during the SLM, which could have caused the residual stresses. A comparison of the partially stress-released SLM specimen and an electron beam melting-manufactured specimen with negligible residual stress suggested that the residual stress caused by the rapid cooling in SLM induced the lattice distortion. This finding is not consistent with the previous understanding that residual stress changes the lattice parameter without lattice distortion. This study provides new insight into lattice distortion generated by a combination of SLM-specific ultrarapid cooling and unstable phases.</p>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: in the metastable β - type Ti - 15Mo - 5Zr - 3Al alloy fabricated by selective laser melting (SLM), whether there is lattice distortion caused by the ultra - rapid cooling and residual stress specific to SLM. Specifically, the research aims to explore the following issues:

1. **Whether lattice distortion is generated during the SLM manufacturing process**:
- Through high - precision X - ray diffractometry (HP - XRD) analysis, the researchers observed that the Ti - 15Mo - 5Zr - 3Al alloy fabricated by SLM exhibits a body - centered - tetragonal (bct) structure instead of the expected body - centered - cubic (bcc) structure. The c - axis is 0.63% shorter than the a - axis.

2. **Whether residual stress is generated during the SLM manufacturing process**:
- XRD analysis also revealed the existence of tensile residual stress of about 210 ± 12 MPa on the specimen surface.

3. **What are the reasons for these phenomena**:
- Numerical simulation indicates that the rapid cooling during the SLM process may be the cause of the residual stress.
- Comparing the SLM specimens with partially released stress and the specimens fabricated by electron beam melting (EBM) (the latter has almost no residual stress), the results show that the residual stress caused by the rapid cooling specific to SLM leads to lattice distortion.

4. **The significance of this finding**:
- This finding is different from the previous understanding, that is, the residual stress not only changes the lattice parameters but also changes the crystal symmetry. This provides new insights into understanding the lattice distortion of metastable phases in AM - processed metal materials.

In summary, this paper aims to reveal the influence of rapid cooling and residual stress on the lattice structure of Ti - 15Mo - 5Zr - 3Al alloy during the SLM manufacturing process and provide a new perspective to understand how these factors work together to cause lattice distortion.