Abstract:To understand and evaluate the thermomechanical property of Ti–6Al–4V alloy prepared by the 3D laser deposition technology, an uniaxial compression test was performed on cylindrical samples using an electronic universal testing machine and enhanced Hopkinson technique, over the range of strain rate from 0.001/s to 5000/s, and at initial temperatures from the room temperature to 1173K. The microstructure of the undeformed and deformed samples was examined through optical microscopy and the use of scanning electron microscope (SEM). The experimental results show the followings: (1) the anisotropy of the mechanical property of this alloy is not significant despite the visible stratification at the exterior surfaces; (2) initial defects, such as the initial voids and lack of fusion, are found in the microstructure and in the crack surfaces of the deformed samples, and they are considered as a major source of crack initiation and propagation; (3) adiabatic shear bands and shearing can easily develop at all selected temperatures for samples under compression; (4) the yield and ultimate strengths of this laser-deposited Ti–6Al–4V alloy are both lower than those of the Ti–6Al–4V alloy prepared by forging and electron beam melting, whereas both of its strengths are higher than those of a conventional grade Ti–6Al–4V alloy at high strain rate only. In addition to compression tests we also conducted tensile loading tests on the laser-deposited alloy at both low and high strain rates (0.1/s and 1000/s). There is significant tension/compression asymmetry in the mechanical response under high-strain-rate loading. It was found that the quasi-static tensile fracturing exhibits typical composite fracture characteristic with quasi-cleavages and dimples, while the high-strain-rate fracturing is characterized by ductile fracture behavior.

In-Situ Tensile Deformation Behavior Of As-Built Laser Direct Metal Deposited Ti-6al-4v Alloy At 200 Degrees C

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

In-situ Comparison of Deformation Behavior at 23 ℃ and 650 ℃ of Laser Direct Melting Deposited Ti-6Al-4V Alloy

Microstructural and texture evolution investigation of laser melting deposited TA15 alloy at 500?C using in-situ EBSD tensile test

Investigating the microstructural evolution during deformation of laser additive manufactured Ti–6Al–4V at 400 °C using in-situ EBSD

In-situ Observation of Temperature Effect on the Tensile Deformation Behavior in Laser Melting Deposited TA15 Alloy

In Situ Electron Backscatter Diffraction Study of Deformation Inhomogeneity under Uniaxial Tension of Laser Melting Deposited TA15 Alloy

Hot Tensile Deformation Behavior of Ti-6Al-4V Titanium Alloy Made by Laser Melting Deposition

Microstructure Evolution and Mechanical Behavior of Laser Melting Deposited TA15 Alloy at 500 °C under In-Situ Tension in SEM

Effect of thermal exposure on microstructure and tensile properties of laser deposited Ti60A alloy

In-Situ SEM Study on Deformation and Failure Mechanism of TC4 Titanium Alloy by Laser Additive Manufacturing

In Situ Investigation of the Tensile Deformation of Laser Welded Ti2alnb Joints

Mechanical Behavior and Fracture Characteristics of Simultaneously Tensile Loaded and Laser Heated Ti6Al4V Alloy

Thermomechanical response of 3D laser-deposited Ti–6Al–4V alloy over a wide range of strain rates and temperatures

Anisotropic Tensile Behavior of Ti-47Al-2Cr-2Nb Alloy Fabricated by Direct Laser Deposition

The Shear Properties and Failure Mechanism of TC11 Titanium Alloy Fabricated by Laser Melting Deposition Technology

Deformation and Fracture Behaviors of Ti6Al4V Alloy Fabricated by Laser Powder Bed Fusion under Combined Tension and Shear Loading

Effect of Heat Treatment on Microstructure and Mechanical Properties of Laser Deposited Ti60A Alloy

Effect of thermal exposure on microstructure and mechanical properties of Ti65 high-temperature titanium alloy deposited by laser direct energy deposition

High strain rate response of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si titanium alloy fabricated by laser additive manufacturing

In Situ Tensile Observation of the Effect of Annealing on Fracture Behavior of Laser Additive Manufactured Titanium Alloy