Abstract:Heat treatment is the most common method to relieve residual stress and to adjust tensile properties in additively manufactured material. However, the well-known strengthening factors (e.g., dislocation density, cellular sub- structure, low angle grain boundaries, nano-oxide particle) in selective laser melted 316 L (SLM 316 L) are strongly influenced by heat-treatment temperature. In this work, horizontal and vertical oriented SLM 316 L specimens are heat treated from 550 degrees C to 1150 degrees C, followed by tensile tests and microstructural characteriza- tion. With increasing temperature, strength (e.g., yield strength, ultimate tensile strength) is found to decrease and elongation is found to increase. The heat treatments of 550 degrees C, 650 degrees C and 750 degrees C lead to coarsening of cellular sub-structure. Furthermore, the cellular sub-structure and melt boundaries annihilate at 950 degrees C. When the temperature reaches 1150 degrees C, SLM 316 L has finished recrystallization with volume fraction of nano-oxide particles increasing greatly. Based on microstructural characterization, the proposed relationship, considering strengthening mechanisms of cellular sub-structure, nano-oxide particle and grain boundaries, give satisfactory accuracy to predict yield strength for horizontal orientation. The yield strength for vertical orientation can also be predicted by this relationship when modified by consideration of anisotropy of columnar grains and lack-of- fusion defects. The anisotropy and lack-of-fusion lead to 5.4% reduction in yield strength for the vertical orientation. This work establishes quantitative relationships for heat treatment-microstructure-property, in which the anisotropy of tensile properties is considered.

Deformation effect of melt pool boundaries on the mechanical property anisotropy in the SLM AlSi10Mg

Role of Melt Pool Boundary Condition in Determining the Mechanical Properties of Selective Laser Melting AlSi10Mg Alloy

Effect of the Boundary Orientation of Melt Pool on Mechanical Property and Fracture Path in Selective-Laser-Melted AlSi10Mg Alloy

Evolution of Heterogeneous Microstructure and its Effects on Tensile Properties of Selective Laser Melted AlSi10Mg Alloy

Effect of Molten Pool Boundaries on the Mechanical Properties of Selective Laser Melting Parts

How Heterogeneous Microstructure Determines Mechanical Behavior of Laser Powder Bed Fusion AlSi10Mg

Effect of microstructural evolution on mechanical properties and fracture modes of AlSi10Mg blocks fabricated by selective laser melting after stress relief annealing

Anisotropy of Microstructure and Tensile Properties of AlSi10Mg Formed by Selective Laser Melting

Damage Mechanisms in Selective Laser Melted AlSi10Mg under As Built and Different Post-Treatment Conditions

Effect of bimodal microstructure on the tensile properties of selective laser melt Al-Mg-Sc-Zr alloy

Process Optimization and Mechanical Property Evolution of AlSiMg0.75 by Selective Laser Melting

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

Microstructure and Anisotropic Mechanical Properties of Selective Laser Melted Ti6Al4V Alloy under Different Scanning Strategies

Impacts of Defocusing Amount and Molten Pool Boundaries on Mechanical Properties and Microstructure of Selective Laser Melted AlSi10Mg

Orientation dependency for microstructure, geometric accuracy and mechanical properties of selective laser melting AlSi10Mg lattices

Influence of Manufacturing Geometric Defects on the Mechanical Properties of AlSi10Mg Alloy Fabricated by Selective Laser Melting

Effect of Processing Parameters on Tensile Properties and Microstructure of Selective Laser Melted AlSi10Mg Alloy

Effect of Heat Treatment on the Anisotropy in Mechanical Properties of Selective Laser Melted AlSi10Mg

Microstructure, porosity and mechanical properties of selective laser melted AlSi10Mg

In-situ tensile testing of fracture and strain in a selective laser melted AlSi10Mg alloy

The Effect of Silicon Phase Morphology on Microstructure and Properties of AlSi10Mg Alloys Fabricated by Selective Laser Melting