Effect of microstructural evolution on mechanical properties and fracture modes of AlSi10Mg blocks fabricated by selective laser melting after stress relief annealing

Jianzhu Li,Yujie Li,Zhe Wang,Changguang Li,Hai Yuan,Yun Hao

DOI: https://doi.org/10.1002/adem.202200585

IF: 3.6

2022-09-02

Advanced Engineering Materials

Abstract:AlSi10Mg parts fabricated by selective laser melting (SLM) are frequently reported to have heterogeneous microstructures. How this affects the mechanical properties of SLM parts still requires further study. In this work, AlSi10Mg blocks with simple cuboid shape were printed and annealed at 300 °C. Their microstructure changes significantly from edge to center and from top to bottom. Low temperature annealing is not sufficient to eliminate structural heterogeneity. Before annealing, the Si‐rich phase is fine and mainly exists in the form of a eutectic network. The as‐printed blocks had high tensile strength, and the fracture surface exhibits a mix of transcellular pits and pores. After annealing, the network structure was completely broken or disappeared in most locations in the blocks. The Si‐rich phase is significantly coarsened and even segregated locally along the melt pool boundaries. Yield strength was reduced by 25‐47%, but elongation values were doubled. Tensile samples were fractured by an along‐the‐pool boundary fracture mode along the boundary. Micropores formed during the printing process were aggregated in the about 200 μm thick outer surface layer of the block. They also have a significant effect on the local elongation both before and after annealing. This article is protected by copyright. All rights reserved.

materials science, multidisciplinary