Abstract:The addition of Sc and Zr into an Al–Mg–Mn alloy produced by selective laser melting exhibited exceptional properties. Multiple factors eventually lead to the improvement of properties, such as densification behaviors, grain characteristics, texture and the precipitated phases. We firstly investigate evolution of the melt pool characteristics which are varied under different processing parameters and lead to different solidified microstructures, densification behaviors and corresponding mechanical properties. Meanwhile, the characteristics of melt pool can be predicted through the normalized enthalpy of input energy, which presents more credible relationship with the melt pool dimensions. To this end, the relative density is up to 99.88% when the volume energy density and normalized enthalpy are combined used. Recrystallisation inhabitations induced by the added Sc and Zr is supposed after comparing the grain sizes under different conditions. Regrettably, the relationship between melt pool characteristics and the equiaxed/columnar ratio can not be described accurately, which due to the pseudo-equiaxed regions in XZ/YZ sections through regulating the melt track orientations via 67° scanning rotation. There are dispersed Al6Mn and Al3(Sc, Zr) particles exist in as-fabricated samples result in better mechanical properties and the subsequent aging treatment can further improve the comprehensive mechanical properties. Finally, the ultimate tensile strength and ductility is separately about 494.32 ± 4.16 MPa and 15 ± 1.27% after aging for 4 h at 325 °C. In contrast, the processing parameters have little impact on mechanical properties, especially for the yield strength, mainly owing to the homologous precipitate phase and grain sizes when the relative density is similar. The connection involving the whole periods from solidification to the final mechanical properties is discussed that may offer feasible ideas for alloy design and corresponding parameter optimization.

Developing a high-strength Al-Mg-Si-Sc-Zr alloy for selective laser melting: Crack-inhibiting and multiple strengthening mechanisms

Microstructures and tensile properties of a selective laser melted Al–Zn–Mg–Cu (Al7075) alloy by Si and Zr microalloying

Microstructure and mechanical properties of Al-Fe-Sc-Zr alloy additively manufactured by selective laser melting

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Microstructural evolution and strengthening mechanism of high-strength AlSi8.1 Mg1.4 alloy produced by selective laser melting

Superior mechanical properties of a selective-laser-melted AlZnMgCuScZr alloy enabled by a tunable hierarchical microstructure and dual-nanoprecipitation

Additive manufacturing of a high strength Al-5Mg2Si-2Mg alloy: Microstructure and mechanical properties

Selective laser melting of Al-3.48Cu-2.03Si-0.48Sc-0.28Zr alloy: Microstructure evolution, properties and metallurgical defects

Microstructure, metallurgical defects and hardness of Al–Cu–Mg–Li–Zr alloy additively manufactured by selective laser melting

Cracking Behavior, Microstructure and Properties of Selective Laser Melted Al-Mn-Mg-Sc-Zr Alloy

Thermal and mechanical properties of an Al-Mg-Sc-Zr high strength alloy fabricated by selective laser melting

Selective laser melting additive manufacturing of 7xxx series Al-Zn-Mg-Cu alloy: Cracking elimination by co-incorporation of Si and TiB2

Selective Laser Melting of Gas Atomized Al–3.02Mg–0.2Sc–0.1Zr Alloy Powder: Microstructure and Mechanical Properties

Achieving high strength in selective laser melting AlSi10Mg alloy by adding microsized pure Cu particles

Tensile property and microstructure of Al−4.77Mn−1.37Mg−0.67Sc−0.25Zr alloy under different selective laser melting processing parameters

Selective laser melting Al-3.4Mg-0.5Mn-0.8Sc-0.4Zr alloys: From melting pool to the microstructure and mechanical properties

Si-Assisted Solidification Path and Microstructure Control of 7075 Aluminum Alloy with Improved Mechanical Properties by Selective Laser Melting

Selective Laser Melted High Mg‐Content Al–Si–Mg–Zr Aluminum Alloy with the Formation of Stacking Faults

Development of a high strength Zr/Sc/Hf-modified Al-Mn-Mg alloy using Laser Powder Bed Fusion: Design of a heterogeneous microstructure incorporating synergistic multiple strengthening mechanisms

A Novel Two-Stage Heat Treatment with Medium-Temperature Aging Influence on Microstructure, Al3(Sc, Zr) Nanoprecipitation, and Application Properties, Enhancing Selective Laser Melting of Al–Mg–Sc–Zr Alloy

A high-strength AlSiMg1.4 alloy fabricated by selective laser melting