Abstract:Additive manufacturing (AM) technology for metallic alloys such as laser powder bed fusion (LPBF) brings tremendous opportunities for development of novel alloys specifically designed for AM that would desensitize the inherent process variability and requires a refined understanding of processing–structure–property relationship that would contribute to future alloy development. In this study, two different alloys, Al-6Zn-2Mg and Al-6Zn-2Mg-0.7Sc-0.3Zr in wt. pct, representing traditional and AM-specific novel aluminum alloys, respectively, were manufactured by LPBF technique using pre-alloyed gas atomized powders. The Al-Zn-Mg ternary alloys exhibited cracks at various LPBF processing parameters, primarily along the grain boundaries of the large columnar grains that extended across multiple melt pools. The severity of cracking in LPBF Al-Zn-Mg alloys was process-dependent and could be correlated to the change in alloy composition due to evaporation of Zn and Mg with high vapor pressure. The Scheil–Gulliver non-equilibrium solidification calculations showed that the Al-Zn-Mg alloys with lower Zn and Mg concentrations had smaller solidification range (i.e., ΔT) and steepness values (i.e., dT/dfs1/2$$ \left| {{\text{d}}T / {\text{d}}f_{\text{s}}^{1/2} } \right| $$ near fs1/2=1$$ f_{\text{s}}^{1/2} = 1 $$), which corresponded to a lower cracking severity. On the other hand, no cracks were observed in Al-Zn-Mg-Sc-Zr alloys, although their solidification range and steepness values were similar to the ternary Al-Zn-Mg alloys. The microstructure of Al-Zn-Mg-Sc-Zr alloys exhibited a much refined heterogeneous microstructure containing small equiaxed and columnar grains within each melt pool, owing to the heterogeneous nucleation upon primary Al3(Sc,Zr) particles. Process-dependent microstructure was observed as a result of variation in thermal gradient and cooling rate associated with LPBF parameters. Findings from this study provide guidance for the future design of AM-specific aluminum alloys and insights into the microstructural control by LPBF.

Selective Laser Melting of Gas Atomized Al–3.02Mg–0.2Sc–0.1Zr Alloy Powder: Microstructure and Mechanical Properties

Selective laser melting of Al-3.48Cu-2.03Si-0.48Sc-0.28Zr alloy: Microstructure evolution, properties and metallurgical defects

Microstructure and mechanical properties of Al-Fe-Sc-Zr alloy additively manufactured by selective laser melting

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Selective laser melting Al-3.4Mg-0.5Mn-0.8Sc-0.4Zr alloys: From melting pool to the microstructure and mechanical properties

Tensile property and microstructure of Al−4.77Mn−1.37Mg−0.67Sc−0.25Zr alloy under different selective laser melting processing parameters

Densification, microstructure and properties of Sc and Zr modified Al-Mn alloy prepared by selective laser melting

Developing a high-strength Al-Mg-Si-Sc-Zr alloy for selective laser melting: Crack-inhibiting and multiple strengthening mechanisms

Microstructure and Mechanical Properties of an Er-Modified Al–Mg–Mn–Sc–Zr Alloy Processed by Selective Laser Melting

A Novel Two-Stage Heat Treatment with Medium-Temperature Aging Influence on Microstructure, Al3(Sc, Zr) Nanoprecipitation, and Application Properties, Enhancing Selective Laser Melting of Al–Mg–Sc–Zr Alloy

Thermal and mechanical properties of an Al-Mg-Sc-Zr high strength alloy fabricated by selective laser melting

Microstructural Evaluation and Tensile Properties of Al-Mg-Sc-Zr Alloys Prepared by LPBF

Microstructure, metallurgical defects and hardness of Al–Cu–Mg–Li–Zr alloy additively manufactured by selective laser melting

Microstructures and tensile properties of a selective laser melted Al–Zn–Mg–Cu (Al7075) alloy by Si and Zr microalloying

The Microstructure and Properties of an Al-Mg-0.3Sc Alloy Deposited by Wire Arc Additive Manufacturing

Mechanical Properties of High Mg-Content Al-Mg-Sc-Zr Alloy Fabricated by Selective Laser Melting

Effect of Processing Parameters on Tensile Properties and Microstructure of Selective Laser Melted AlSi10Mg Alloy

Cracking Behavior, Microstructure and Properties of Selective Laser Melted Al-Mn-Mg-Sc-Zr Alloy

Selective Laser Melting of Al-Cu-Mn-Mg Alloys: Processing and Mechanical Properties

Process-Dependent Composition, Microstructure, and Printability of Al-Zn-Mg and Al-Zn-Mg-Sc-Zr Alloys Manufactured by Laser Powder Bed Fusion

The effect of a remelting treatment scanning strategy on the surface morphology, defect reduction mechanism, and mechanical properties of a selective laser-melted Al-based alloy