Effect of adding ways of calcium zirconate on performance of MgO-CaZrO3 based dispersed porous refrac-to ry
Jiegang You,Zhipeng Xie,Yiwei Cao,Guodong Zhang
DOI: https://doi.org/10.3969/j.issn.1001-1935.2016.02.003
2016-01-01
Abstract:In order to improve the performance of magnesia dispersed porous refractory,high-purity magne-sia particles (0.2 -1 mm),pre-synthesized calcium zirconate powder (≤0.074 mm),analytically pure cal-cium carbonate powder (≤0.044 mm)and monoclinic zirconia powder (≤0.005 mm)were used as start-ing materials to design the formulations based on 87 mass% high purity magnesia and 13 mass% calcium zirconate in the fired specimens.The different calcium carbonate adding ways were adopted:pre-synthe-sized calcium zirconate,in-situ formed calcium zirconate by the reaction between calcium carbonate and zirconia,and pre-synthesized calcium zirconate plus in-situ formed calcium zirconate.After batching,mix-ing,molding,drying at 110 ℃ and firing at 1 650 ℃ for 3 h,the apparent porosity,bulk density,gas permea-bility,thermal shock resistance,cold and hot strengthes,and microstructure of the specimens were investi-gated.The results show:with the increase of the in-situ formed calcium zirconate,the linear shrinkage rate, apparent porosity and gas permeability increase;cold crushing strength,cold modulus of rupture,hot mod-ulus of rupture,and thermal shock resistance increase initially and then decrease;and the distribution of calcium zirconate becomes more uniform.The complex adding of pre-synthesized calcium zirconate and in-situ formed calcium zirconate is optimum for the gas permeability,cold strength,hot strength,and ther-mal shock resistance.