Abstract:The composite ceramics between Al 2 O 3 (6 mol%MgO) and ZrO 2 (4 mol%Y 2 O 3 ) were prepared in the Al 2 O 3 (6 mol%MgO added: ZrO 2 (4 mol%Y 2 O 3 added) ratios of 20:80, 35:65, 50:50, 65:35 and 80:20. All of samples were sintered using two stage sintering routes with the first temperature (T 1 ) at 1600 °C for 30 min and the second temperature (T 2 ) at 1450 °C for 5 h. The physical properties were characterized from percentage of shrinkage and bulk density. It can be found their tend to decrease with Al 2 O 3 (6 mol%MgO) content increase. XRD patterns were showed combination main phase of rhombohedral of Al 2 O 3 and monoclinic, cubic, tetragonal of ZrO 2 . Rietveld refinement were used to calculate the percentage of phase composition. All of samples were revealed weight percentage of main composition as m -ZrO 2 c -ZrO 2 t -ZrO 2 and r - Al 2 O 3 in different ratios. It can be found, sample with more content of ZrO 2 was showed higher weight percentage of c -ZrO 2 . The high intensity of Al 2 O 3 peak was appeared from sample with high Al 2 O 3 concentration. SEM micrographs reveal morphology of grain such as grain shape and size of grains. The average grain size value is between 0.81 and 1.07 μm and the size of grain tend to increase with high Al 2 O 3 content. EDX technique were analyzed element compositions of Al 2 O 3 (6 mol%MgO): ZrO 2 (4 mol%Y 2 O 3 ) and EDX spectra were showed wt.% element of Al, Zr, O Y and Mg which is confirmed molecular formular. Moreover, EDX method is identified square shape of Al 2 O 3 (6 mol%MgO) and round shape of ZrO 2 (4 mol%Y 2 O 3 ). The mechanical properties were measured by Vickers and Knoop hardness that were used for calculating the fracture toughness value. It can be found that the optimum mechanical properties were obtained from composite ceramic of 0.35Al 2 O 3 (6 mol%MgO): 0.65ZrO 2 (4 mol%Y 2 O 3 ) which is showed the highest of fracture toughness value about 0.38 GPa.m 1/2 .

Role of t-ZrO2 stabilization methods in phase composition, structure and properties of ZTA ceramics

The Effect of Al2O3 on the Thermal Stability and Mechanical Properties of 3Y-TZP

Sintering Behavior and Mechanical Properties of Alumina-Coated Zirconia Ceramics

Influence of Y2O3 Doping on Phase Evolution and Dielectric Characteristics of ZrO2 Ceramics

Effect of Dy2O3 content on microstructure and mechanical properties of zirconia-toughened alumina

Zirconia Toughened Alumina Ceramics via Forming Intragranular Structure

Thermophysical and mechanical properties of cubic, tetragonal and monoclinic ZrO2

Stabilization of phase‐pure tetragonal zirconia ceramics with minimum CeO2 doping and associated benefits

The Study on Degradation of Y<sub>2</sub>O<sub>3</sub>-CeO<sub>2</sub>-Partially Stabilized ZrO<sub>2</sub> Adding Al<sub>2</sub>O<sub>3</sub> Particles at Low Temperature

Effect of Ceria Doping on the Mechanical Properties and Phase Stability of Partially Samaria-Stabilized Zirconia Crystals

Research of Structural, Strength and Thermal Properties of ZrO2—CeO2 Ceramics Doped with Yttrium

Effect of Al2O3 on the Phase Stability of Y-Ce-TZP/Al2O3 Composites at Low Temperature

Microstructure and mechanical properties of dense ZTA ceramics with high Cr2O3 solution

Impact of chemical and physical modification of zirconia on structure, surface state, and catalytic activity in oxidation of α-tetralol

Hardness and Indentation Fracture Toughness of Slip Cast Alumina and Alumina-Zirconia Ceramics

Hydrothermal Synthesis of Nanocrystalline ZrO2-8Y2O3-xLn2O3 Powders (Ln = La, Gd, Nd, Sm): Crystalline Structure, Thermal and Dielectric Properties

Preparation and Characterization of Alumina Zirconia Composite Ceramics

Study of Factors Influencing the Microstructure and Phase Content of Ultrafine Y-Tzp

Phase transformation of Y-Ce-TZP/Al2O3 composite ceramic annealed in air

Few-monolayer yttria-doped zirconia films: Segregation and phase stabilization

Phase and microstructure evolution of 0.2Zr1-Ce O2/Zr1-Ce SiO4 (0 ≤ x + y ≤ 1) ceramics designed to immobilize tetravalent actinides