Effect of Dy2O3 content on microstructure and mechanical properties of zirconia-toughened alumina

Yu Zhang,Yudong Sui,Yehua Jiang,Lina Han

DOI: https://doi.org/10.1016/j.ceramint.2022.04.304

IF: 5.532

2022-04-01

Ceramics International

Abstract:In this study, the effect of adding Dy2O3 on the microstructure and mechanical properties of zirconia-toughened alumina (ZTA) stabilised by yttrium oxide was investigated. ZTA-Dy2O3 composites with different Dy2O3 contents (0 wt%, 1 wt%, 2 wt%, 3 wt%, and 4 wt%) were prepared by sintering at 1600 °C for 4 h. The phases and structures of the samples were characterised through X-ray diffraction (XRD) and scanning electron microscopy (SEM). Dy2O3 formed a solid solution c-DYZ with YSZ, and an appropriate amount of Dy2O3 could refine the grains and contribute to densification. The densities, hardness, flexural strength and toughness all increased and then decreased with increasing Dy2O3 content, reaching maximum values of 99.2%, 1741 ± 19 HV, 449 ± 10 MPa and 5.87 ± 0.42 MPa‧m1/2, respectively, at 3 wt% Dy2O3 content.

materials science, ceramics