Abstract:The composite ceramics between Al 2 O 3 (6 mol%MgO) and ZrO 2 (4 mol%Y 2 O 3 ) were prepared in the Al 2 O 3 (6 mol%MgO added: ZrO 2 (4 mol%Y 2 O 3 added) ratios of 20:80, 35:65, 50:50, 65:35 and 80:20. All of samples were sintered using two stage sintering routes with the first temperature (T 1 ) at 1600 °C for 30 min and the second temperature (T 2 ) at 1450 °C for 5 h. The physical properties were characterized from percentage of shrinkage and bulk density. It can be found their tend to decrease with Al 2 O 3 (6 mol%MgO) content increase. XRD patterns were showed combination main phase of rhombohedral of Al 2 O 3 and monoclinic, cubic, tetragonal of ZrO 2 . Rietveld refinement were used to calculate the percentage of phase composition. All of samples were revealed weight percentage of main composition as m -ZrO 2 c -ZrO 2 t -ZrO 2 and r - Al 2 O 3 in different ratios. It can be found, sample with more content of ZrO 2 was showed higher weight percentage of c -ZrO 2 . The high intensity of Al 2 O 3 peak was appeared from sample with high Al 2 O 3 concentration. SEM micrographs reveal morphology of grain such as grain shape and size of grains. The average grain size value is between 0.81 and 1.07 μm and the size of grain tend to increase with high Al 2 O 3 content. EDX technique were analyzed element compositions of Al 2 O 3 (6 mol%MgO): ZrO 2 (4 mol%Y 2 O 3 ) and EDX spectra were showed wt.% element of Al, Zr, O Y and Mg which is confirmed molecular formular. Moreover, EDX method is identified square shape of Al 2 O 3 (6 mol%MgO) and round shape of ZrO 2 (4 mol%Y 2 O 3 ). The mechanical properties were measured by Vickers and Knoop hardness that were used for calculating the fracture toughness value. It can be found that the optimum mechanical properties were obtained from composite ceramic of 0.35Al 2 O 3 (6 mol%MgO): 0.65ZrO 2 (4 mol%Y 2 O 3 ) which is showed the highest of fracture toughness value about 0.38 GPa.m 1/2 .

Fabrication and Mechanical Properties of Homogeneous Zirconia Toughened Alumina Ceramics Via Cyclic Solution Infiltration and in Situ Precipitation

Zirconia Toughened Alumina Ceramics via Forming Intragranular Structure

A study of mechanical properties of alumina–zirconia composite films prepared by a combination of tape casting and solution impregnation method

ZrSiO4 toughed Al2O3 ceramics prepared by reaction sintering

Sintering Behavior and Mechanical Properties of Alumina-Coated Zirconia Ceramics

Effect of zirconia sol on the microstructure and properties of Al2O3-based ceramic fabricated from natural bauxite

Hardness and Indentation Fracture Toughness of Slip Cast Alumina and Alumina-Zirconia Ceramics

Preparation and Characterization of Alumina Zirconia Composite Ceramics

Effect of Dy2O3 content on microstructure and mechanical properties of zirconia-toughened alumina

Fabrication of High-Performance Al2O3-ZrO2 Composite by a Novel Approach That Integrates Stereolithography-Based 3D Printing and Liquid Precursor Infiltration

Preparation, mechanical properties, and toughening mechanisms of SiCw/SiCp‐reinforced zirconia‐toughened alumina ceramics

Preparation and Performance for Zirconia/Alumina Composite Ceramics

Microstructure and mechanical properties of dense ZTA ceramics with high Cr2O3 solution

Microstructure and mechanical properties of Zr3Al3C5-based ceramics synthesized by Al-Si melt infiltration

A novel method for fabricating brick-mortar structured alumina-zirconia ceramics with high toughness

Mechanical properties and wear behaviors of Cu-doped zirconia-toughened alumina ceramics

[Study of relationship between powder-size gradation and mechanical properties of Zirconia toughened glass infiltrated nanometer-ceramic composite powder]

Effectively Inhibiting Abnormal Grain Growth of Alumina in ZTA with Low‐Content Fine‐Sized ZrO2 Inclusions Introduced by Infiltration and in Situ Precipitation

Effects of Zircon Additive on the Properties of 95-Alumina Ceramic

The Rising Crack Resistance Curve Behavior and Mechanism of La2O3 Doped Zirconia Toughened Alumina Composites Prepared Via Vat Photopolymerization Based 3D Printing

Synergistic Toughening Effect of SiC Whiskers and Particles in ZrO2–Al2O3–SiC Ceramics