Abstract:Alumina (Al2O3) based ceramics are widely used for making machine parts, high-temperature components, wear-resistant material and biological ceramic due to their high hardness, strength, wear-resistance, and chemical and thermal stability. However, low fracture toughness (KIC∼3.0 MPa.m1/2) inhibit its usage in other potential applications where high toughness is a pre-requisite (e.g. ceramic engine). In an attempt to improve the strength, particularly the fracture toughness, two step sintering process was used. Sintering temperature was optimized based on the results obtained from dilatometer and DSC-TG analysis. X-ray fluorescence (XRF) was used to make compositional analysis of as received raw powders and X-ray Diffraction (XRD) was used to analysis the phase purity and crystallinity for both powder and sintered samples. Microstructure was investigated by using SEM. Hardness and fracture toughness was measured and its correlation with microstructure was investigated. Density was measured by Archimedes method and crystalline density from XRD. Microhardness diamond indenter was used and the diagonal length of indent and the crack lengths were measured by SEM to calculate the Vickers hardness values and fracture toughness, respectively. The maximum fracture toughness was obtained 4.03 MPa.m1/2 for Al2O3 ceramic and the hardness value was 15.97 GPa. Density was found 99.6% of the relative density of Alumina at optimum sintering cycle and the grain size was found 0.38 µm. Thermal expansion coefficient was measured by dilatometer and the calculated value was 7.9×10-6 K-1. The physical properties of the Alumina were good enough and comparable to withstand high temperature applications.

A novel method for fabricating brick-mortar structured alumina-zirconia ceramics with high toughness

Facile method for preparing lamellar structured alumina-zirconia ceramics with high toughness

Cost-effective Fabrication of Bio-Inspired Nacre-Like Composite Materials with High Strength and Toughness

Fabrication and Characterisation of Alumina/aluminium Composite Materials with a Nacre-Like Micro-Layered Architecture

Preparation and Mechanical Behavior of Si3N4 Composite Ceramics with Brick‐and‐mortar Structure

Preparation and mechanical behavior of Si 3 N 4 composite ceramics with brick‐and‐mortar structure

Towards high strengthening efficiency of equiaxed and platelet-shaped alumina reinforced zirconia ceramics with textured microstructure using DLP-based stereolithography

Enhanced Mechanical Properties in Ceramic Multilayer Composites Through Integrating Crystallographic Texture and Second-Phase Toughening

Method for preparing biomimetic ceramic structures with high strength and high toughness

R-curve of La2O3 doped Zirconia Toughened Alumina Composites Prepared via Stereolithography based 3D Printing

A Novel Processing Route to Develop Alumina Matrix Nanocompositesreinforced with Multi-Walled Carbon Nanotubes

ZrO 2 Matrix Toughened Ceramic Material‐Strength and Toughness

ZrO2 Matrix Toughened Ceramic Material‐Strength and Toughness

Biomimetic structure design — a possible approach to change the brittleness of ceramics in nature

Fabrication and Mechanical Properties of Homogeneous Zirconia Toughened Alumina Ceramics Via Cyclic Solution Infiltration and in Situ Precipitation

Zirconia Toughened Alumina Ceramics via Forming Intragranular Structure

Ultratough conductive graphene/alumina nanocomposites

The Rising Crack Resistance Curve Behavior and Mechanism of La2O3 Doped Zirconia Toughened Alumina Composites Prepared Via Vat Photopolymerization Based 3D Printing

Synthesis, Evaluation And Characterization Of Alumina Ceramics With Elongated Grains

Optimization of sintering profile to achieve highly toughened alumina based ceramic

Zirconia-based Nanocomposite Toughened by Functionalized Multi-Wall Carbon Nanotubes