Effect of MgO addition on properties of reaction-sintered ZrO2-toughened Al2O3 multiphase ceramic

Liwang Wang,Jiabang Wang,Hui Yang

DOI: https://doi.org/10.3969/j.issn.1001-1935.2005.06.004

2005-01-01

Refractories

Abstract:Zirconia-toughened Al2O3 composite ceramic was prepared using zircon powder and α-Al2O3 powder as main starting materials and adding MgO as sintering aids and stabilizer off-ZrO2 by in-situ reaction sintering at 1500°C for 4 h, 1550°C for 4 h,1600°C for 4 h and 1650°C for 4 h respectively. It was shown that the added MgO had promoted the sintering of the ceramic and increased the content of t-ZrO2. Meanwhile, MgO had affected resultant phases and inhibited the formation of mullite. In multiphase ceramic with 5wt% ZrO2 by doping ZrSiO4, and the addition of MgO accounted for 8% of ZrO2 addition, the ceramic sintered at 1600°C had the maximum cold MOR of 220 MPa and the fracture toughness of 6.2 MPa·m1/2.