Abstract:Objectives To investigate transient thermal stresses that developed in 3Y-TZP green compacts during speed sintering. Methods A total of 312 disc-shaped green compacts (Ø17.1 ×1, 1.5, 2, 2.5, 3 mm) were cold-isostatically pressed from 3Y-TZP powder (Zpex, Tosoh Corp.) for speed sintering studies as well as compositional analysis and biaxial flexural strength measurements (both at room temperature and following heating at 90 °C/min to 500 °C). Flexural strength was determined using the piston-on-3-ball method. Phase assemblies were analyzed using the X-ray diffraction method. Effects of heating/cooling rates on transient stresses were investigated by conducting definitive sintering studies to determine the threshold for fracture. Finite element analysis (FEA) was used to validate the experimental findings using measured thermomechanical properties. Results The bulk and relative density of the green compact were 2.95 ± 0.03 g/cm 3 and 48.52% ± 0.45%. The flexural strength was drastically decreased from 10.3 ± 0.4 MPa to 1.09 ± 0.07 MPa following heating at 90 °C/min to 500 °C. The monoclinic and tetragonal contents were 54.9% and 45.1%, respectively. The threshold for fracture was located at 500 °C during the first heating stage with a 90 °C/min heating rate in specimens of 2.5 mm thickness or greater. No fractures occurred in the second heating stage and cooling phase. The FEA estimated that the principal transient tensile stress was ∼1.14 MPa at 500 °C during the heating phase, which exceeded the corresponding flexural strength (1.09 ± 0.07 MPa). Significance Advanced FEA methods are an accurate and efficient tool to analyze the history of transient stresses during sintering of ceramic dental restorations.

Effect of Sintering Time on the Stability of Y2O3 Partially Stabilized Zirconia

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

Cubic Yttria Stabilized Zirconia Sintering Additive Impacts: A Comparative Study

Formation and Rate Processes of Y2o3 Stabilized Zro2 Thin Films from Zr(Dpm)(4) and Y(Dpm)(3) by Cold-Wall Aerosol-Assisted Mocvd

Microstructural dependence of aging induced phase transformation in Y2O3 partially stabilized ZrO2 polycrystals

Study of Factors Influencing the Microstructure and Phase Content of Ultrafine Y-Tzp

Fracture Toughness of Al2O3‐Particle‐Dispersed Y2O3‐Partially Stabilized Zirconia

Raman and X-ray photoelectron spectroscopic characterizations of thermal stability of 3 mol% yttria stabilized zirconia ceramics

Effect of Y2O3 Contents and Grain Sizes on the Mechanical Properties and Transformation of Zirconia Ceramics at Cryogenic Temperatures

Microstructures and Mechanical Properties of Sr2Nb2O7-toughened 3Y-TZP Ceramics

Influence of Y2O3 Doping on Phase Evolution and Dielectric Characteristics of ZrO2 Ceramics

Transient thermal stresses developed during speed sintering of 3 mol% yttria-stabilized tetragonal zirconia polycrystals

Mechanical Properties Durability of Sc2O3-Y2O3 Co-Stabilized ZrO2 Thermal Barrier Materials for High Temperature Application

The Effect of Al2O3 on the Thermal Stability and Mechanical Properties of 3Y-TZP

Effect of Dy2O3 content on microstructure and mechanical properties of zirconia-toughened alumina

Mechanical properties and low temperature degradation (LTD) of cation-stabilized zirconia

The Effect of Sintering Temperature on Phase-Related Peculiarities of the Microstructure, Flexural Strength, and Fracture Toughness of Fine-Grained ZrO2–Y2O3–Al2O3–CoO–CeO2–Fe2O3 Ceramics

Properties of a Pressureless Sintered 2Y-TZP Material Combining High Strength and Toughness

High Temperature Mechanical Properties of Zirconia Metastable T '-Phase Degraded Yttria Stabilized Zirconia

Initial sintering mechanism and additive effect in zirconia ceramics

Effect of Sintering Temperature on Compressive Strength of Porous Yttria-Stabilized Zirconia Ceramics