The phase stability of t-ZrO2 realized by grain size at cryogenic temperature in ZrO2/TiO2 composite
Huan Li,Weifeng Qian,Zhen Zhang,Shuang Wang,Yongnan Chen,Fengying Zhang,Zhimin Hou,Guangrui Gao,Qinyang Zhao,Haifei Zhan
DOI: https://doi.org/10.1016/j.matdes.2024.112741
IF: 9.417
2024-03-01
Materials & Design
Abstract:In this work, the trade-off between transformation toughening of ZrO2/TiO2 ceramic coatings and low temperature (293.15 K∼203.15 K) was achieved by adjusting the grain size of t-ZrO2 ( d t - Z r O 2 ). A negative correlation between d t - Z r O 2 and phase transition temperature (Ms ) was also established based on strain energy and chemical free energy in ZrO2/TiO2 ceramic coatings. Interestingly, t-ZrO2 grains lost toughening effects when the d t - Z r O 2 reaches the critical size (20 nm) even under cooling and stress. This is attributed to the number of dislocations per unit volume increases 1.5 times with the d t - Z r O 2 decreases from 40 nm to 20 nm, which aggravates the lattice distortion and dislocation tangle and leads to the fracture toughness increases by 32.5% at 203.15 K. Therefore, the interfacial cohesion of the semi-coherent interface between (011) t-ZrO2 and (110) TiO2 was enhanced and t-ZrO2 was completely stabilized when d t - Z r O 2 reaches critical size. This work elucidates the effect of size effect on Ms and provides a reference for transformation toughening of ceramic coatings at cryogenic temperature.
materials science, multidisciplinary