Abstract:The aim of this study was to investigate the low-temperature degradation (LTD) kinetics of tetragonal zirconia with 3 mol% yttria (3Y-TZP) dental ceramic using two degradation methods: hydrothermal degradation and immersed degradation. To study transformation kinetics, we prepared 3Y-TZP powders. We pressed these powders uniaxially into a stainless mold at 100 MPa. We then sintered the compacted bodies at intervals of 50 °C between 1300 °C and 1550 °C and immersed the specimens at various temperatures from 60 °C to 80 °C in 4% acetic acid or from 110 °C to 140 °C for the hydrothermal method. We used a scanning electron microscope (SEM) to confirm crystalline grain size and used X-ray diffraction to analyze the zirconia phase. As the sintering temperature increased, the calculated crystalline grain size also increased. We confirmed this change with the SEM image. The higher sintering temperatures were associated with more phase transformation. According to the Mehl-Avrami-Johnson equation, the activation energies achieved using the hydrothermal method were 101 kJ/mol, 95 kJ/mol, and 86 kJ/mol at sintering temperatures of 1450 °C, 1500 °C, and 1550 °C, respectively. In addition, the activation energies of the specimens immersed in 4% acetic acid were 60 kJ/mol, 55 kJ/mol, 48 kJ/mol, and 35 kJ/mol, with sintered temperatures of 1400 °C, 1450 °C, 1500 °C, and 1550 °C, respectively. The results showed that a lower sintering temperature would restrain the phase transformation of zirconia because of the smaller crystalline grain size. As a result, the rate of LTD decreased.

Critical effect of cubic phase on aging in 3 mol% yttria-stabilized zirconia ceramics for hip replacement prosthesis

Cubic Yttria Stabilized Zirconia Sintering Additive Impacts: A Comparative Study

[Study on Low Temperature Degradation of Dental Zirconia Ceramic].

Modeling the aging kinetics of zirconia ceramics

Accelerated Aging in 3 mol%-Yttria-Stabilized Tetragonal Zirconia Ceramics Sintered in Reducing Conditions

Microstructural dependence of aging induced phase transformation in Y2O3 partially stabilized ZrO2 polycrystals

Low-temperature ageing of zirconia-toughened alumina ceramics and its implication in biomedical implants

Percolative Mechanism of Aging in Zirconia-Containing Ceramics for Medical Applications

Influence of Low Temperature Aging on the Flexural Strength of Y-TZP Ceramics

Raman and X-ray photoelectron spectroscopic characterizations of thermal stability of 3 mol% yttria stabilized zirconia ceramics

Zirconia ageing is related to total hip arthroplasty aseptic loosening. A study of 45 retrieved zirconia heads

Effect of accelerated aging on dental zirconia-based materials

Microstructural investigation of the aging behavior of $(3Y-TZP)-Al_2O_3$ composites

Evaluation of Feasibility on Dental Zirconia-Accelerated Aging Test by Chemical Immersion Method

Yttrium effect on 475 °C brittleness of Fe–13Cr–6Al–2Mo-0.5Nb-0.15Zr alloy

High Temperature Mechanical Properties of Zirconia Metastable T '-Phase Degraded Yttria Stabilized Zirconia

Effect of Al2O3 on Degradation of 3Y-TZP Ceramics at Low Temperature

Effects of Low-Temperature Aging on Mechanical Properties of Two Kinds of Dental Zirconia Ceramics

Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics

Atomic force microscopy study of the tetragonal to monoclinic transformation behaviour of silica doped yttria-stabilized zirconia

The Effect of Sintering Temperature on the Microstructure and Phase Transformation in Tetragonal YSZ and LZ/YSZ Composites