Microstructures and Mechanical Properties of Sr2Nb2O7-toughened 3Y-TZP Ceramics

XQ Liu,XM Chen

DOI: https://doi.org/10.1016/s0272-8842(02)00211-0

IF: 5.532

2003-01-01

Ceramics International

Abstract:The effects of sintering time upon microstructures and the mechanical properties were investigated for Sr2Nb2O7-toughened 3Y-TZP ceramics. The incorporation of Sr2Nb2O7 secondary phase significantly enhanced the fracture toughness of 3Y-TZP ceramics, and the toughening effect was noticeably influenced by sintering conditions through microstructural changes: the fracture toughness increased with increasing soaking time for compositions of xless than or equal to0.01, but a slight decrease of fracture toughness with soaking time was observed for x 0.015, where x is the mole fraction of Sr2Nb2O7. The high fracture toughness, K-1C, of 13.7 MPa m(1/2), was achieved in the ceramic with x = 0.005 sintered at 1500 degreesC for 6 h. This is almost a doubling of fracture toughness, compared to the specimens without Sr2Nb2O7. It should be emphasized that the high fracture toughness, K-1C of 10 MPa m(1/2)(1.4 times that of the matrix) could be obtained even for the situation without transformable tetragonal phase where the phase transition toughening was not active and the piezoelectric/ferroelectric secondary phase played an important role. (C) 2003 Elsevier Ltd and Techna S.r.l. All rights reserved.