Abstract:Al2O3 coatings, which can be produced by plasma electrolytic oxidation (PEO) on aluminum substrates, provide an excellent protection against corrosion and wear. However, due to the brittle nature of the oxide ceramic, the fracture toughness is limited. One approach to enhance the tolerance to fracture is the incorporation of ZrO2 to form zirconia toughened alumina (ZTA). In addition to its use as a bulk material, the application as a coating material enables a broader field of application. In this study, an Al2O3-ZrO2 composite coating was applied on a 6082 aluminum alloy using an aluminate-phosphate-based electrolytic solution containing a Zr-based salt. Polarization measurement as an indicator of the passivability of a given system revealed that Zr-based salt improves the passivation of the aluminum alloy. The coatings' characteristics were evaluated by SEM, EDS, and XRD. ZrO2 incorporated into alumina as a metastable high-temperature modification led to a thicker coating with new morphologies including lamellar and dendritic structures. Nano-indentation showed that the incorporated Zr increase the average hardness of the compact layer from 16 GPa to 18 GPa. The fracture toughness of the coatings was investigated locally with nano-scratches applied on the compact outer layer of the coatings' cross-sections. The Zr-containing electrolytic solution resulted in a coating with significantly higher fracture toughness (6.9 MPa∙m1/2) in comparison with the Zr-free electrolytic solution (4.6 MPa∙m1/2). Therefore, it is shown, that the PEO process stabilized a high-temperature allotrope of zirconia at room temperature without the need for rare-earth dopants such as Y2O3. Furthermore, it was demonstrated that the nano-scratch method is a suitable and accurate technique for the investigation of the fracture toughness of coatings with inherent cracks.

Fracture Toughness of Al2O3‐Particle‐Dispersed Y2O3‐Partially Stabilized Zirconia

Effect of Sintering Time on the Stability of Y2O3 Partially Stabilized Zirconia

Toughening of Ti3SiC2 with 3Y-TZP addition by spark plasma sintering

Zirconia-based Nanocomposite Toughened by Functionalized Multi-Wall Carbon Nanotubes

Effect of TZP nanoparticles synthesized by RCVD on mechanical properties of ZTA composites sintered by SPS

ZrSiO4 toughed Al2O3 ceramics prepared by reaction sintering

Effect of Dy2O3 content on microstructure and mechanical properties of zirconia-toughened alumina

Effects of Sr2Nb2O7 additive on microstructure and mechanical properties of 3Y–TZP/Al2O3 ceramics

Properties of a Pressureless Sintered 2Y-TZP Material Combining High Strength and Toughness

Characterization of nano ceramic composite of Mullite-Magnesia-Yttria stabilized Zirconia system

The Rising Crack Resistance Curve Behavior and Mechanism of La2O3 Doped Zirconia Toughened Alumina Composites Prepared Via Vat Photopolymerization Based 3D Printing

Enhanced Toughness Of Zirconia Ceramics With Graphene Platelets Consolidated By Spark Plasma Sintering

Al 2 O 3 -fiber-reinforced porous YSZ ceramics with high mechanical strength

Assessing fracture toughness in sintered Al2O3–ZrO2(3Y)–SiC ceramic composites through indentation technique

A novel method for fabricating brick-mortar structured alumina-zirconia ceramics with high toughness

Effect of ball milled Zr/Al/ZrB2 composite powders on microstructure and toughening of ZrB2–SiC/Zr–Al–C composite ceramics sintered by spark plasma sintering

[Study of relationship between powder-size gradation and mechanical properties of Zirconia toughened glass infiltrated nanometer-ceramic composite powder]

Enhanced thermal shock resistance of ZrO2-reinforced Al2O3–CaAl12O19 composites prepared from ferrotitanium slag: Crack propagation resistance mechanisms

Evaluation of Fracture Toughness of Plasma Electrolytic Oxidized Al2O3-ZrO2 Coatings Utilizing Nano-Scratch Technique

Microstructure and electrical properties of aluminum oxide‐reinforced 3 mol% yttria‐stabilized tetragonal zirconia polycrystals/TiSi2 composites by vacuum sintering

Comparison of sintering behavior and reinforcing mechanisms between 3Y-TZP/Al2O3(w) and 12Ce-TZP/Al2O3(w) composites: Combined effects of lanthanide stabilizer and Al2O3 whisker length