Towards high strengthening efficiency of equiaxed and platelet-shaped alumina reinforced zirconia ceramics with textured microstructure using DLP-based stereolithography
Yang Wang,Qingxuan Zhou,Zhuoqun Han,Yongning Han,Lunan Bi,Xia Zhang,Xiang Lu,Jie Zhao,Wei Chu,Jian Li,Zhicheng Zhao,Yingying Wang,Jia Liu,Ling Li,Futian Liu
DOI: https://doi.org/10.1016/j.ceramint.2023.11.039
IF: 5.532
2023-12-04
Ceramics International
Abstract:ZrO 2 –Al 2 O 3 (ATZ) ceramics are attracting high interest in biomedical applications because of their desirable mechanical performance and biocompatibility. However, strength and toughness are mutually exclusive in structural ceramics. In this paper, based on digital light processing, novel textured ATZ ceramics with obvious crystallographic orientations were fabricated by incorporating Al 2 O 3 platelets with a high aspect ratio and equiaxed particles into the ZrO 2 matrix. The optimized fracture toughness of 16.9 ± 0.8 MPa m 1/2 was achieved in the textured ATZ ceramic, which was about 67.3 % higher than non-textured ZrO 2 ceramics, without sacrificing strength. The coupling toughening effects of macrolayer structure, equiaxed and platelet-shaped Al 2 O 3 particles, and ZrO 2 particles were responsible for the enhanced mechanical performance. The macroscale toughening of 3D-printed lamellar architecture led to effective energy dissipation. Additionally, the crack deflection and crack branching induced by dual-morphology Al 2 O 3 particles, accompanied by the phase transformation of the ZrO 2 matrix, were significant microscopic toughening mechanisms.
materials science, ceramics