Abstract:STATEMENT OF PROBLEM: Yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramic material has been reported to possess exceptionally high flexural strength; however, the strength of Y-TZP ceramics can be affected by surface treatments performed by dental laboratory technicians and by intraoral conditions.PURPOSE: This study investigated the influence of low-temperature-degradation (LTD) treatment, airborne-particle abrasion, and polishing on the flexural strength and structural stability of a Y-TZP ceramic material.MATERIAL AND METHODS: By sectioning zirconia ceramic blocks (Vita In-Ceram YZ blocks) into 25 x 4 x 2-mm bars, 310 specimens were fabricated and divided into 9 groups: Group C, as-sintered (control); group B24h, boiled in water for 24 hours; group B7d, boiled in water for 7 days; group H6h, stored in humidified air at 250 degrees C for 6 hours; group H24h, stored in humidified air at 250 degrees C for 24 hours; group H7d, stored in humidified air at 250 degrees C for 7 days; group P, polished; group A, airborne-particle abraded; and group AB, airborne-particle abraded and boiled for 7 days. The flexural strengths (MPa) of all specimens were determined by using a 3-point bending test. The variability was analyzed by using Weibull statistics. Pairwise differences among the 9 groups were evaluated by using confidence intervals (95%) for scale and shape parameters. From every block used, 8 specimens were obtained and every specimen was marked according to the location of its origin from the original block. Surfaces of the specimens were evaluated by using scanning electron microscopy (SEM) at various magnifications. X-ray diffraction analysis was performed to identify possible tetragonal-to-monoclinic phase transformations. Energy dispersive spectroscopy (EDS) was used to obtain information on the chemical composition.RESULTS: Aging or "finishing" treatments had no significant negative effects on flexural strengths. Mean flexural strengths ranged from 796.7 to 950.2 MPa. Group A exhibited the highest mean flexural strength (950.2 MPa). Weibull modulus values ranged between 5.6 and 9.3. Tetragonal-to-monoclinic phase transformation was detected for a specimen boiled for 24 hours. More tetragonal-to-monoclinic phase transformation was detected for specimens boiled for 7 days and stored in humidified air at 250 degrees C for 7 days. The SEM examination of fractured surfaces revealed sintering defects, and EDS analysis showed less yttria concentration on Y-TZP specimens that were boiled for 7 days.CONCLUSION: Within the limitations of this study, the results suggested that the LTD procedures and the polishing treatment used did not reduce the flexural strengths of zirconia bars. Airborne-particle abrasion increased the flexural strength of specimens.CLINICAL IMPLICATIONS: Although polishing, airborne-particle abrasion, and various low-temperature degradation (LTD) treatments did not significantly degrade the strength of the Y-TZP ceramic material, LTD resulted in loss of yttria. Over time, gradual dissolution of yttria could decrease the tetragonal-phase stability and long-term clinical serviceability of this dental ceramic material.

Transient thermal stresses developed during speed sintering of 3 mol% yttria-stabilized tetragonal zirconia polycrystals

[Study on Low Temperature Degradation of Dental Zirconia Ceramic].

Impact of the sintering parameters on the grain size, crystal phases, translucency, biaxial flexural strength, and fracture load of zirconia materials

Current speed sintering and high-speed sintering protocols compromise the translucency but not strength of yttria-stabilized zirconia

Zirconia changes after grinding and regeneration firing

Effect of Sintering Time on the Stability of Y2O3 Partially Stabilized Zirconia

In Vitro Evaluation of Speed Sintering and Glazing Effects on the Flexural Strength and Microstructure of Highly Translucent Multilayered 5 mol% Yttria-Stabilized Zirconia

Effect of Sintering Temperature on Compressive Strength of Porous Yttria-Stabilized Zirconia Ceramics

In vitro evaluation of low-temperature aging effects and finishing procedures on the flexural strength and structural stability of Y-TZP dental ceramics

Effect of rapid cooling on residual stress and surface fracture toughness of dental zirconia

Effect of speed sintering process on the microstructure, flexural strength and translucency of zirconia

Accelerated Aging in 3 mol%-Yttria-Stabilized Tetragonal Zirconia Ceramics Sintered in Reducing Conditions

Effect of grinding parameters on surface integrity and flexural strength of 3Y-TZP ceramic

Infiltration OF 5Y-PSZ with thermally compatible glass: Strength, microstructure and failure mode analyses

The effect of zirconia sintering temperature on flexural strength, grain size, and contrast ratio

Effect of Multistep Processing Technique on the Formation of Micro-Defects and Residual Stresses in Zirconia Dental Restorations.

Slow Crack Growth Behavior of 3Y-TZP in Cryogenic Environment Using Dynamic Fatigue and Indentation Technique

Flexural strength of novel glass infiltrated monochrome and multilayer high yttrium oxide containing zirconia upon various sintered cooling rates

Cyclic fatigue resistance of yttria-stabilized tetragonal zirconia polycrystals with hot isostatic press processing

Effect of the Intaglio Surface Treatment and Thickness of Different Types of Yttria-Stabilized Tetragonal Zirconia Polycrystalline Materials on the Flexural Strength: In-Vitro Study

Mechanical and electrical properties of 3Y‐TZP/TiSi2 composites sintered at different temperatures