Abstract:Fabrication of diode by forming n-type electrical contact on germanium (Ge) and its AC impedance analysis is important for radiation detection in the form of pulses. In this work lithium (Li) metal has been electro-deposited on p-type Ge single crystal from molten lithium nitrate at 260°C. The depth of Li diffusion in Ge was successfully varied by changing the electroplating time as determined by sheet resistance (SR) measurement after successive lapping of Ge surface. Li is found to diffuse up to 500 micron inside Ge by heat treatment of as deposited Li/Ge at 350°C for 1 hour. A stable n-type electrical contact on Ge with SR ~1 ohm/square and impurity concentration ~3.7x10^15/cm^3 is developed by Li incorporation in p-type Ge crystal showing net carrier concentration ~3.4x10^10/cm^3 and SR ~100 Kohm/square. Acceptor concentration determined from the 1/C^2 vs V plot shows similar temperature dependence as found by Hall measurement. The fabricated n+/p junction exhibit ideal diode characteristics with gradual increase in cut off voltage at low temperatures. Under forward bias, junction capacitance mainly comprises of diffusion capacitance (~10 micro.F) showing strong frequency dependence and the impedance is partly resistive resulting in semicircular Cole-Cole plot. Imaginary impedance spectra reveal that the relaxation time for the diffusion of majority carriers decreases at higher temperatures and increased forward voltages. The diode is purely capacitive under reverse bias showing a line parallel to the y-axis in the Cole-Cole plot with frequency independent (100Hz-100MHz) depletion capacitance ~10pF.

p-n Junction revealed by Electrolytic Etching

Electrochemical Pore Etching in N- and P-Type Ge

N-Type Area of PN Junction Etched in BOE Solution

P-N Junction Formation in Electron-beam Irradiated Graphene Step

Ferroelectric Domain Wall p-n Junctions

Monolithic lateral p-n junction GaAs nanowire diodes via selective lateral epitaxy

Direct assessment of p-n junctions in single GaN nanowires by Kelvin probe force microscopy

Impact of Junction Depth and Abruptness on the Activation and the Leakage Current in Germanium n$^{+}$/p Junctions

High Performance Ge Ultra-Shallow Junctions Fabricated by A Novel Formation Technique Featuring Spin-On Dopant and Laser Annealing for Sub-10 Nm Technology Applications

Pristine PN junction toward atomic layer devices

On the Electrochemical Growth of a Crystalline p‐n Junction From Aqueous Solutions

Formation of a p-n junction on the GaAs-surface by an Ar+ ion beam

Direct-Bandgap Electroluminescence from Germanium with Subband Engineering Utilizing a Metal-Oxide-Semiconductor Structure

Fabrication of n+ contact on p-type high pure Ge by cathodic electrodeposition of Li and impedance analysis of n+/p diode at low temperatures

Direct Injection Tunnel Spectroscopy of a P-N Junction

On the Formation of Solid State Crystallized Intrinsic Polycrystalline Germanium Thin Films

P-N Crossed Nanojunctions from Electroless-Etched Si Nanowires

Selective etching of n-type silicon in pn junction structure in hydrofluoric acid and its application in silicon nanowire fabrication.

Seamless Lateral Graphene P–n Junctions Formed by Selective in Situ Doping for High-Performance Photodetectors

Assessment of active dopants and p-n junction abruptness using in-situ biased 4D-STEM

Chemical Impurities and Lattice Defects in High-Purity Germanium