Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Effect of a bimodal grain structure on corrosion behavior and tensile properties of low-alloyed Mg-1Bi-1Zn-1Ag alloy

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effect of Extrusion on Mechanical Property, Corrosion Behavior, and In Vitro Biocompatibility of the As-Cast Mg-Zn-Y-Sr Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Microstructure, Non-Basal Texture and Strength-Ductility of Extruded Mg-6Bi-3Zn Alloy

Microstructure, Mechanical Properties and Corrosion Behavior of Mg-Zn-Zr Alloys with Different Compositions

Microstructure, Mechanical and Corrosion Properties and Biocompatibility of Mg-Y-Zn-Zr Rolled Alloy for Biomedical Applications

Enhancing Strength-Ductility Synergy and Corrosion Residual Strength of Hot-Rolled Mg-2Zn-0.85Y Alloy

A newly developed Mg-Zn-Gd-Mn-Sr alloy for degradable implant applications: Influence of extrusion temperature on microstructure, mechanical properties and in vitro corrosion behavior

Elucidating the dependence of corrosion behavior and mechanical property on the grain structure of low-temperature as-extruded Mg–Zn–Ca–Zr alloy

Mechanical properties and bio-corrosion behavior of Mg-Zn-Zr alloy influenced by rotary swaging

Effect of Extrusion Process on Microstructure, Corrosion Properties, and Mechanical Properties of Micro-Alloyed Mg–Zn–Ca–Zr Alloy

Improvement of Mechanical Properties and Corrosion Resistance of As‐Extruded Mg–2Zn–2Al–0.3Mn Alloy Through Y Addition

Effects of extrusion parameters on the microstructure, corrosion resistance, and mechanical properties of biodegradable Mg–Zn–Gd–Y–Zr alloy

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Anisotropic tensile and degradation properties of as-extruded Mg-6Zn-2Sn-0.5Mn alloy

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy