Abstract:In our previous work, we designed a new as-cast Mg–Y–Zn–Al–Li alloy with a high elastic modulus of 52.9 GPa. The alloy was further subjected to hot deformation under different rolling reductions (40% and 80%) in this work. The microstructure evolution, texture and mechanical properties of Mg–Y–Zn–Al–Li alloy compared with Mg–Y–Zn alloy were systematically investigated. The result showed that the Mg–Y–Zn–Al–Li alloy with a rolling reduction of 40% displayed a more homogeneous fine microstructure and a weakened basal texture, accompanied by the formation of Al–Li and nano-precipitates Al0.9Li34.3Mg64.5Zn0.3 phase. Compared with the Mg–Y–Zn alloy, the strength and ductility of the alloy also were obviously enhanced while possessing a weak mechanical anisotropy. Grain refinement and second phase strengthening (fine Al–Li phase and nano-precipitates Al0.9Li34.3Mg64.5Zn0.3) mainly contributed to the enhanced strength. The texture weakening, low dislocation density and non-basal slip commonly guaranteed the high ductility, especially the weakened texture gave rise to the low anisotropy. When the rolling reduction increased to 80%, the volume fraction of recrystallized grains in Mg–Y–Zn–Al–Li alloy increased significantly to73.3%. As a result, the symmetry of the texture distribution around the ND was appreciably improved. In addition, the lower dislocation density and more non-basal slip in the Mg–Y–Zn–Al–Li alloy with the rolling reduction of 80% further enhanced the ductility. Simultaneously, the anisotropic degree of mechanical was effectively minimized, which was mainly attributed to the weak symmetric texture caused by fine DRXed grains with random misorientation and non-basal pyramidal <c+a> slip.

Enhancing Strength-Ductility Synergy and Corrosion Residual Strength of Hot-Rolled Mg-2Zn-0.85Y Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

High strength-ductility synergy and low anisotropy of Mg-4.5Al-2.6Zn-0.3Mn alloy sheet achieved by annealing after rolling

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Simultaneously Improving Strength and Ductility of Mg−3Li−8Gd−2Y−1.5Ag Alloy by Solution Treatment and Hot‐Rolling Process

Microstructure, Mechanical and Corrosion Properties and Biocompatibility of Mg-Y-Zn-Zr Rolled Alloy for Biomedical Applications

Novel Mg–Al–Sn–Zn–Y Alloys with Enhanced Strength−Ductility Combination Prepared by Hard‐Plate Rolling

Strength-ductility synergy in Mg98.3Y1.3Ni0.4 alloy processed by high temperature homogenization and rolling

Simultaneous improvement of strength and damping capacities of Mg-8Li-6Y–2Zn alloy by heat treatment and hot rolling

A Rolled Mg‐8Al‐1Sm‐1Zn Alloy with High Strength‐Ductility via Single‐Pass Liner Rolling

Microstructure, texture and mechanical properties of the rolled high modulus Mg-Y-Zn-Al-Li alloy

A high-performance Mg-Al-Sn-Zn-Bi alloy fabricated by combining sub-rapid solidification and hot rolling

Development of low-alloyed Mg–Zn–Ca–Sn–Mn alloy with high strength-ductility synergy by sub-rapid solidification and hot rolling

Influence of Hot Rolling on Microstructure, Corrosion and Mechanical Properties of Mg–Zn–Mn–Ca Alloy

High corrosion resistance and weak corrosion anisotropy of an as-rolled Mg-3Al-1Zn (in wt.%) alloy with strong crystallographic texture

High performance Mg-8Gd-4Y-1Zn-0.5Al alloy with long-period stacking ordered structure by hot rolling

Effect of Heat Treatment on Corrosion and Mechanical Properties of Mg-10Y-1.5Zn-0.5Zr Alloy

Improvement of Mechanical Properties and Corrosion Resistance of As‐Extruded Mg–2Zn–2Al–0.3Mn Alloy Through Y Addition