Abstract:High strength-elongation synergy and its dependence on microstructure are the eternal themes of metallic materials including Ti alloys. In this study, the relationship between the microstructure evolution and mechanical properties of the Ti-25Zr-4Al-1.5Mn (TZAM, wt. %) near-α Ti alloy was systematically investigated after hot rolling at temperatures ranging in the whole solid solution region. The content of primary α phase decreased gradually with the increasing of rolling temperature. An excellent comprehensive mechanical properties with a yield strength of 1055±10 MPa and a total elongation of 23.6±0.6% were obtained for the specimen after rolling at 750 °C (single α phase temperature region). This great strength-elongation synergy is mainly due to the synthetic action of substructure strengthening, dislocation strengthening, basal random heterogeneity (BRH) texture, and suitable content of β phase. The α" martensitic phase was formed after rolling at temperatures of 800 and 850 °C (α + β two-phase temperature region), resulting in a significant decrease in yield strength. However, remarkable work hardening with a rate of approximately 10 GPa occurred in both specimens. The whole evolution process of primary α grains, namely dynamic recovery and recrystallization during hot-rolled is deeply discussed. When the rolling temperature increased to 900 °C (single β phase temperature region), the dominated acicular α´ martensitic phase with high dislocation density resulted in an ultra-high strength (1264±12 and 1488±11 MPa for yield and tensile strength respectively) at the expense of plasticity. These findings revealed the microstructure evolution and its relationship to the mechanical properties of a TiZr-based alloy after the thermomechanical processing and helped to understand deeply the theory of metallic strengthening and elongation.

A Rolled Mg‐8Al‐1Sm‐1Zn Alloy with High Strength‐Ductility via Single‐Pass Liner Rolling

Enhancing Mechanical Properties of Rolled Mg-Al-Ca-Mn Alloy Sheet by Zn Addition

Improving the Ductility of Mg-2.5Nd-0.5Zn-0.5Zr Alloy by Multi-Pass Hot Rolling

Microstructure and Tensile Properties of Mg-3Al-1Zn Sheets Produced by Hot-Roller-cold-material Rolling

Improving the mechanical properties of duplex Mg-Li-Zn alloy by mixed rolling processing

Microstructure, texture and mechanical properties of the rolled high modulus Mg-Y-Zn-Al-Li alloy

Microstructure and mechanical property of multi-pass low-strain rolled Mg-Al-Zn-Mn alloy sheet

Microstructure and Mechanical Properties of Rolled Mg-12gd-3y-0.4zr Alloy Sheets

Property Improvements in Fine–grained Mg–Zn–Zr Alloy Sheets Produced by Temperature–step–down Multi–pass Rolling

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

High performance Mg-8Gd-4Y-1Zn-0.5Al alloy with long-period stacking ordered structure by hot rolling

Microstructure Regulation and Strength-Elongation Synergy of the Near Alpha TZAM Alloy Via Thermomechanical Processing

Achieving ultrahigh strength in binary Al-10Mg alloy through heavy cryogenic rolling

Effect of Warm Rolling on the Microstructure, Texture and Mechanical Properties of Extruded Mg–Zn–Ca–Ce/La Alloy

A high-performance Mg-Al-Sn-Zn-Bi alloy fabricated by combining sub-rapid solidification and hot rolling

Non-basal Slips Mediated Dynamic Recrystallization Promote Synergistic Strengthening and Toughening of Centrifugal Casting Mg–1.1Mn–0.5Al Alloy via High Strain Rolling

Effect of Dual Deformation Processes on the Microstructure and Mechanical Properties of Low-Alloyed Mg-Zn-Ca-Mn Alloy

Dynamic recrystallization, texture and mechanical properties of high Mg content Al–Mg alloy deformed by high strain rate rolling

Achieving enhanced mechanical properties in the Mg–Y–Zn–V alloy by refining grains and improving the morphology and distribution of LPSO via pre-forging and subsequent rolling

Enhancing Strength-Ductility Synergy and Corrosion Residual Strength of Hot-Rolled Mg-2Zn-0.85Y Alloy

Strength Enhancement of Mg–3Gd–1Zn Alloy by Cold Rolling