Abstract:In our previous work, we designed a new as-cast Mg–Y–Zn–Al–Li alloy with a high elastic modulus of 52.9 GPa. The alloy was further subjected to hot deformation under different rolling reductions (40% and 80%) in this work. The microstructure evolution, texture and mechanical properties of Mg–Y–Zn–Al–Li alloy compared with Mg–Y–Zn alloy were systematically investigated. The result showed that the Mg–Y–Zn–Al–Li alloy with a rolling reduction of 40% displayed a more homogeneous fine microstructure and a weakened basal texture, accompanied by the formation of Al–Li and nano-precipitates Al0.9Li34.3Mg64.5Zn0.3 phase. Compared with the Mg–Y–Zn alloy, the strength and ductility of the alloy also were obviously enhanced while possessing a weak mechanical anisotropy. Grain refinement and second phase strengthening (fine Al–Li phase and nano-precipitates Al0.9Li34.3Mg64.5Zn0.3) mainly contributed to the enhanced strength. The texture weakening, low dislocation density and non-basal slip commonly guaranteed the high ductility, especially the weakened texture gave rise to the low anisotropy. When the rolling reduction increased to 80%, the volume fraction of recrystallized grains in Mg–Y–Zn–Al–Li alloy increased significantly to73.3%. As a result, the symmetry of the texture distribution around the ND was appreciably improved. In addition, the lower dislocation density and more non-basal slip in the Mg–Y–Zn–Al–Li alloy with the rolling reduction of 80% further enhanced the ductility. Simultaneously, the anisotropic degree of mechanical was effectively minimized, which was mainly attributed to the weak symmetric texture caused by fine DRXed grains with random misorientation and non-basal pyramidal <c+a> slip.

Effect of Warm Rolling on the Microstructure, Texture and Mechanical Properties of Extruded Mg–Zn–Ca–Ce/La Alloy

Effect of Dual Deformation Processes on the Microstructure and Mechanical Properties of Low-Alloyed Mg-Zn-Ca-Mn Alloy

Microstructure, Mechanical Properties and Texture Evolution of Mg–Al–Zn–La–Gd–Y Magnesium Alloy by Hot Extrusion and Multi-Pass Rolling

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

Insights into the evolution of texture and mechanical properties during warm rolling and annealing of Mg–2Zn-0.5Ca alloy

Strengthening Mg–8Li–3Al–2Zn-1Gd-0.2Zr alloy by combining hot extrusion and cold rolling

Achieving High Strength in Micro-alloyed Mg-Al-Ca-Zn-Mn-Ce Alloy Sheet Processed by Single-Pass Large-Strain Rolling

Effect of Rolling Reduction on the Microstructure and Mechanical Properties of Hot-Rolled Mg-Li-Al-Ca Alloys

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Improved Ductility of Mg–Zn–Ce Alloy by Hot Pack-Rolling

Effects of Single-Pass Large-Strain Rolling on Microstructure and Mechanical Properties of Mg-Al-Ca Alloy Sheet

Microstructure Evolution and Mechanical Properties of High-Strength Mg-Gd-Y-Zn-Mn Alloy Processed by Asymmetric Hot Rolling

Effect of the Rolling Process on Microstructures and Mechanical Properties of the Extruded LA91 Alloy Sheet

Effect of Rolling Strain on Microstructure and Tensile Properties of Dual-Phase Mg–8Li–3Al–2Zn–0.5Y Alloy

Effect of Large Strain Cross Rolling on Microstructure and Properties of Al−Li Alloy Plates with High Magnesium Content

Effect of rolling temperature on deformation behavior and mechanical properties of Mg-8Li-1Al-0.6Y-0.6Ce alloy

Effect of Hot-Rolling on Microstructures and Mechanical Properties of Extruded Mg-6gd-3.2y-Xzn-0.5zr Sheet

Effect of Rolling with Different Amounts of Deformation on Microstructure and Mechanical Properties of the Mg–1Al–4Y Alloy

Microstructure, texture and mechanical properties of the rolled high modulus Mg-Y-Zn-Al-Li alloy

Strengthening of Mg-Li Alloy Dominated by Continuously Hardened Mg Phase During Room Temperature Rolling

Improving the mechanical properties of duplex Mg-Li-Zn alloy by mixed rolling processing