Abstract:In our previous work, we designed a new as-cast Mg–Y–Zn–Al–Li alloy with a high elastic modulus of 52.9 GPa. The alloy was further subjected to hot deformation under different rolling reductions (40% and 80%) in this work. The microstructure evolution, texture and mechanical properties of Mg–Y–Zn–Al–Li alloy compared with Mg–Y–Zn alloy were systematically investigated. The result showed that the Mg–Y–Zn–Al–Li alloy with a rolling reduction of 40% displayed a more homogeneous fine microstructure and a weakened basal texture, accompanied by the formation of Al–Li and nano-precipitates Al0.9Li34.3Mg64.5Zn0.3 phase. Compared with the Mg–Y–Zn alloy, the strength and ductility of the alloy also were obviously enhanced while possessing a weak mechanical anisotropy. Grain refinement and second phase strengthening (fine Al–Li phase and nano-precipitates Al0.9Li34.3Mg64.5Zn0.3) mainly contributed to the enhanced strength. The texture weakening, low dislocation density and non-basal slip commonly guaranteed the high ductility, especially the weakened texture gave rise to the low anisotropy. When the rolling reduction increased to 80%, the volume fraction of recrystallized grains in Mg–Y–Zn–Al–Li alloy increased significantly to73.3%. As a result, the symmetry of the texture distribution around the ND was appreciably improved. In addition, the lower dislocation density and more non-basal slip in the Mg–Y–Zn–Al–Li alloy with the rolling reduction of 80% further enhanced the ductility. Simultaneously, the anisotropic degree of mechanical was effectively minimized, which was mainly attributed to the weak symmetric texture caused by fine DRXed grains with random misorientation and non-basal pyramidal <c+a> slip.

Strengthening Mg–8Li–3Al–2Zn-1Gd-0.2Zr alloy by combining hot extrusion and cold rolling

Effect of Warm Rolling on the Microstructure, Texture and Mechanical Properties of Extruded Mg–Zn–Ca–Ce/La Alloy

Microstructure, Mechanical Properties and Texture Evolution of Mg–Al–Zn–La–Gd–Y Magnesium Alloy by Hot Extrusion and Multi-Pass Rolling

Strength Enhancement of Mg–3Gd–1Zn Alloy by Cold Rolling

Improving the mechanical properties of duplex Mg-Li-Zn alloy by mixed rolling processing

Reducing the yield asymmetry in Mg-5Li-3Al-2Zn alloy by hot-extrusion and multi-pass rolling

Microstructures and mechanical properties of high-strength Mg-Gd-Y-Zn-Zr alloy sheets processed by severe hot rolling

Improving the corrosion resistance of Mg-8Li-3Al-2Zn alloy by combining Gd alloying and hot extrusion

Microstructure, texture and mechanical properties of the rolled high modulus Mg-Y-Zn-Al-Li alloy

Microstructure Evolution and Strengthening Mechanism of Dual-Phase Mg–8.3Li–3.1Al–1.09Si Alloys during Warm Rolling

Effect of Dual Deformation Processes on the Microstructure and Mechanical Properties of Low-Alloyed Mg-Zn-Ca-Mn Alloy

A Rolled Mg‐8Al‐1Sm‐1Zn Alloy with High Strength‐Ductility via Single‐Pass Liner Rolling

Microstructural evolution and enhanced mechanical properties of Mg–Gd–Y–Zn–Zr alloy via centrifugal casting, ring-rolling and aging

Effect of Cold Deformation on Microstructure and Mechanical Properties of Mg-8Gd-3Y-0.5Zr Alloy

Effect of final rolling deformation on microstructure, work hardening and softening behavior of Mg-8Li-3Al-0.3Si alloys

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

Achieving enhanced mechanical properties in the Mg–Y–Zn–V alloy by refining grains and improving the morphology and distribution of LPSO via pre-forging and subsequent rolling

Microstructure and Mechanical Properties of Rolled Mg-12gd-3y-0.4zr Alloy Sheets

Simultaneously Improving Strength and Ductility of Mg−3Li−8Gd−2Y−1.5Ag Alloy by Solution Treatment and Hot‐Rolling Process

Simultaneous Improvement of Strength, Ductility and Damping Capacity of Single Β-Phase Mg-Li-Al-Zn Alloys

Effect of cold rolling on the microstructure and mechanical properties of MG-8GD-3Y-0.5ZR alloy