Abstract:The basal texture of traditional magnesium alloy AZ31 is easy to form and exhibits poor plasticity at room temperature. To address these problems, a multi-micro-alloyed high-plasticity Mg–1.8Zn–0.8Gd–0.1Ca–0.2Mn (wt%) alloy was developed using the unique role of rare earth and Ca solute atoms. In addition, the influence of the annealing process on the grain size, second phase, texture, and mechanical properties of the warm-rolled sheet at room temperature was analyzed with the goal of developing high-plasticity magnesium alloy sheets and obtaining optimal thermal-mechanical treatment parameters. The results show that the annealing temperature has a significant effect on the microstructure and properties due to the low alloying content: there are small amounts of larger-sized block and long string phases along the rolling direction (RD), as well as several spherical and rodlike particle phases inside the grains. With increasing annealing temperature, the grain size decreases and then increases, and the morphology, number, and size of the second phase also change correspondingly. The particle phase within the grains vanishes at 450°C, and the grain size increases sharply. In the full recrystallization stage at 300–350°C, the optimum strength-plasticity comprehensive mechanical properties are presented, with yield strengths of 182.1 and 176.9 MPa, tensile strengths of 271.1 and 275.8 MPa in the RD and transverse direction (TD), and elongation values of 27.4% and 32.3%, respectively. Moreover, there are still some larger-sized phases in the alloy that influence its mechanical properties, which offers room for improvement.

Effect of pack-rolling temperature on microstructure and mechanical properties of Mg-6Sn-3Al-1Zn Alloy

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Effects of Hot Rolling Processing on Microstructures and Mechanical Properties of Mg–3%Al–1%Zn Alloy Sheet

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys

Effect of rolling temperature on deformation behavior and mechanical properties of Mg-8Li-1Al-0.6Y-0.6Ce alloy

Microstructure and mechanical property of multi-pass low-strain rolled Mg-Al-Zn-Mn alloy sheet

Deformation Microstructure and Characteristics of Cast-Rolling and Normal Rolling AZ31 Magnesium Alloy Sheets

Effect of Warm Rolling on the Microstructure, Texture and Mechanical Properties of Extruded Mg–Zn–Ca–Ce/La Alloy

Effects of Per-Pass Reduction and Annealing Treatment on Microstructures and Mechanical Properties of Mg-Zn-Ce-Zr Alloy

Influence of Hot Rolling on Microstructure, Corrosion and Mechanical Properties of Mg–Zn–Mn–Ca Alloy

Effects of rolling processing on the microstructures, mechanical properties and strain softening behavior of biodegradable Zn-0.06 Mg alloy

Effect of Cold Deformation on Microstructure and Mechanical Properties of Mg-8Gd-3Y-0.5Zr Alloy

Effect of Aging Treatment on Microstructure and Damping Properties of Mg-Al-Ca-Mn-Zn Alloy

Revealing the Microstructure Evolution Mechanism and Mechanical Responses of a Novel Al–Zn–Mg–Cu Alloy by Hot Deformation Process

Rolling Temperature and Subsequent Annealing on Microstructure, Texture and Mechanical Properties of Consecutive Rolled Mg-2.0zn-0.8gd Alloy

Microstructure and Mechanical Properties of Hot-Rolled Mg-Zn-Y-Zr Magnesium Alloy

Effect of Rolling Deformation on Microstructure and Mechanical Properties of As-Cast and Rolled ZM21 Magnesium Alloy

Effect of Rolling Temperature on Microstructure and Properties of Al-Mg-Li Alloy

Microstructure and Mechanical Properties of Rolled Mg-12gd-3y-0.4zr Alloy Sheets

Effect of cold rolling on the microstructure and mechanical properties of MG-8GD-3Y-0.5ZR alloy

Microstructure, Hot Deformation Behavior, and Recrystallization Behavior of Zn-1Fe-1Mg Alloy under Isothermal Compression