Abstract:Microstructure, texture evolution and mechanical properties of extruded Mg-4.58Zn-2.6Gd-0.18Zr alloy were investigated at extrusion temperatures of 260 °C, 280 °C and 300 °C, extrusion ratios of 10, 15 and 30, and ram speeds of 3 mm s−1 and 6 mm s−1, respectively. The results indicated that the as-cast experimental alloy was composed of α-Mg matrix, coarse α-Mg + W(Mg3Zn3Gd2) eutectic and icosahedral quasicrystalline I(Mg3Zn6Gd) phase. A small amount of undissolved W phases were detected after the homogenization treatment at 505 °C up to 16 h, while most I phase dissolved into the α-Mg matrix. The initial crystallites before extrusion were randomly oriented, and showed a typical random texture. After extrusions, all samples exhibited a bimodal microstructure consisting of fine Dynamic recrystallization (DRX) grains and coarse elongated un-DRX grains, and the formation of ultra-fine DRX grains only occurred in the sample with an extrusion ratio of 10 at 260 °C, 3 mm s−1, which was caused by the solute segregation in homogenized billets and non-uniformly distributed W phase during the extrusion process. A fiber texture with {0002} planes and <1̄21̄0> directions paralleled to the extrusion direction was observed to be dominant in all the extruded samples. Furthermore, the increase of extrusion ratio was found to be beneficial for the DRX process and refinement of grain size, and the maximum texture intensity was accordingly weakened, which resulted in a decrease of tensile yield strength but an increase of elongation. With increasing the extrusion temperature or ram speed, both the grain size and DRX fraction gradually increased. Consequently, the texture was randomized and the maximum texture intensity decreased, which led to a reduction of the elongation and tensile yield strength. The tensile failure behaviors under different extrusion conditions were found to be related with the contraction twin lamellas formed in the un-DRX grains and the string-like W phases.

Anisotropic tensile and degradation properties of as-extruded Mg-6Zn-2Sn-0.5Mn alloy

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Evolution of Microstructure and Tensile Properties of Extruded Mg-4Zn-1Y Alloy

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Microstructures and Mechanical Properties of As-Extruded and Heat Treated Mg–6Zn–1Mn–4Sn–1.5Nd Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

Microstructure, Texture Evolution and Tensile Properties of Extruded Mg-4.58Zn-2.6Gd-0.16Zr Alloy

Microstructures and mechanical properties of extruded and aged Mg–Zn–Mn–Sn–Y alloys

Microstructure, Tensile Properties and Work Hardening Behavior of an Extruded Mg–Zn–Ca–Mn Magnesium Alloy

In Vitro Degradation Behavior and Cytocompatibility of Mg-6Zn-Mn Alloy

Microstructure, Non-Basal Texture and Strength-Ductility of Extruded Mg-6Bi-3Zn Alloy

Microstructure and Mechanical Properties of Extruded Mg–1Ca–1Zn–0.6Zr Alloy

Effect of Extrusion on Mechanical Property, Corrosion Behavior, and In Vitro Biocompatibility of the As-Cast Mg-Zn-Y-Sr Alloy

Modulation of corrosion properties by heat treatment and extrusion with mechanism analysis of high mechanical strength Mg-5.6Dy-3.1Ni alloy

Evolution of the Microstructure and Mechanical Properties of Mg-10Gd-2Y-0.5Zn-0.3Zr Alloy during Extrusion and Aging Processes

Microstructure and Mechanical Properties of an Extruded Mg-2Dy-0.5Zn Alloy

Anisotropy and Deformation Mechanisms ofAs-Extruded Mg-3Zn-1Y Magnesium AlloyUnder High Strain Rates

A newly developed Mg-Zn-Gd-Mn-Sr alloy for degradable implant applications: Influence of extrusion temperature on microstructure, mechanical properties and in vitro corrosion behavior

Mechanical properties and creep properties of a dilute hot-extruded Mg-Mn-Zn alloy sheet with an ED-tilted texture

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion