Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Zijian Yu,Linlin Liu,Adil Mansoor,Ke Liu,Shubo Li,Wenbo Du

DOI: https://doi.org/10.1016/j.jallcom.2021.158826

IF: 6.2

2021-05-01

Journal of Alloys and Compounds

Abstract:<p>In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg₃RE phase variants, which are bulk Mg₃RE phase with a size range of 10–30 µm, spot Mg₃RE phase with a size range of 1–2 µm and spherical Mg₃RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg₃RE phase has a strong dispersion strengthening effect, while the bulk Mg₃RE phase acts as crack resources and deteriorates the ductility. A novel island-like <span class="math"><math>β1R</math></span> phase (FCC, <em>a</em> = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <span class="math"><math>(1̅12)β1R</math></span>//<span class="math"><math>(101̅0)α</math></span> interface at the broad facet and a semi-coherent <span class="math"><math>(1̅11)β1R</math></span>//<span class="math"><math>(112̅0)α</math></span> interface at the end facet. The <span class="math"><math>β1R</math></span> phase transforms from <span class="math"><math>βH</math></span> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <span class="math"><math>β1R</math></span> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <span class="math"><math>β1R</math></span> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg₃RE phase variants, and <span class="math"><math>β1R</math></span> phase.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to improve the mechanical properties of Mg - Li alloys. In particular, a new Mg - 8Gd - 2Y - 1Zn - 6Li (GWZL8216) alloy was designed and prepared by adding Li to the traditional high - strength Mg - Gd - Y - Zn alloy. The research aims to deeply explore the influence of different intermetallic compounds on the microstructure and mechanical properties, and gain in - depth understanding of the strengthening mechanism of the GWZL8216 alloy. In addition, for the first time, this work reported a new nano - scale metastable phase found in the extruded GWZL8216 alloy, explored its formation mechanism, and analyzed in detail its crystallographic characteristics and strengthening effect.

Specifically, the paper focuses on the following aspects:
1. **Alloy composition and treatment process**: The Mg - 8Gd - 2Y - 1Zn - 6Li alloy was prepared by casting, heat treatment, and hot extrusion processes, and the influence of these processes on the microstructure and mechanical properties of the alloy was studied.
2. **Microstructure analysis**: The microstructure of the alloy was analyzed in detail by means of optical microscopy (OM), field - emission scanning electron microscopy (FE - SEM), high - angle annular dark - field scanning transmission electron microscopy (HAADF - STEM), and X - ray diffraction (XRD), including the different morphologies and distributions of the α - Mg phase, β - Li phase, and Mg₃RE phase.
3. **Discovery of a new metastable phase**: A new island - like metastable phase R1 phase was discovered for the first time, and its crystallographic characteristics, formation mechanism, and influence on the mechanical properties of the alloy were explored.
4. **Mechanical property evaluation**: The yield strength (TYS), tensile strength (UTS), and elongation (EL) of the alloy were tested and compared with those of the traditional Mg - Li alloys, showing its superior strength - plasticity balance.
5. **Aging behavior study**: The aging behavior of the alloy at different temperatures was studied, and it was found that the dissolution of the R1 phase during the aging process led to the softening phenomenon of the alloy.

Through the above research, the paper aims to provide theoretical basis and technical support for the development of high - performance Mg - Li alloys.