Crystal structure, phase content, and tensile properties of As-cast Mg–Gd–Y–Al alloys

Xiqin Liu,Fang Liu,Zili Liu,Huanjian Xie,Jian Li

DOI: https://doi.org/10.1016/j.mtcomm.2020.101286

IF: 3.8

2020-12-01

Materials Today Communications

Abstract:<p>The lattice parameters, phase content, and tensile properties of as-cast Mg–<em>x</em>Gd–(4–<em>x</em>)Y–2Al (<em>x</em> = 0, 2, 4) alloys were investigated via X-ray diffraction, Rietveld refinement, scanning electron microscopy, and transmission electron microscopy. The Mg-RE phase, Al₂RE phase, and Al₁₁RE₃ phase occurred in all three alloys. Furthermore, the cell volume and axial ratio (<em>c/a</em>) of the α-Mg matrix decreased with increasing (0–4 wt.%) Gd content. The abundance of the Al₂RE and Mg-RE phases decreased with increasing Gd content, whereas that of the Al₁₁RE₃ phase increased. Moreover, Al₂RE particles formed at the grain centers served as active nucleation sites, thereby leading to grain refinement, and acicular Al₁₁RE₃ phases restricted the growth of α-Mg. The tensile properties improved with increasing Gd content. In fact, the optimal mechanical properties (yield strength: 77.83 MPa, ultimate tensile strength: 195.01 MPa, and elongation: 15.71 %) were obtained for the Mg–4Gd–2Al alloy. Furthermore, strengthening of the material occurred mainly via second-phase strengthening and solid-solution strengthening. Block Al₂RE particles can cut the matrix during the stretching process, and the acicular Al₁₁RE₃ phase may play a major role in enhancing the tensile properties. In addition, the ductility of the alloy system improved with decreasing axial ratio (<em>c/a</em>).</p>

materials science, multidisciplinary

What problem does this paper attempt to address?

This paper mainly discusses the lattice parameters, phase composition, and tensile properties of Mg-xGd-(4-x)Y-2Al casting alloy. The effects of different Gd contents (0%, 2%, 4%) on the alloy were analyzed through methods such as X-ray diffraction, Rietveld refinement, scanning electron microscopy, and transmission electron microscopy. The results showed that with the increase of Gd content, the lattice parameters and the c/a ratio of α-Mg matrix decreased, while the quantities of Al2RE and Mg-RE phases decreased and the quantity of Al11RE3 phase increased. The Al2RE particles formed in the grain center acted as active nucleation sites, resulting in grain refinement, while the needle-like Al11RE3 phase restricted the growth of α-Mg, thus improving the tensile properties of the alloy. With the increase of Gd content, the mechanical properties of the alloy (such as yield strength, tensile strength, and elongation) were also enhanced, especially Mg-4Gd-2Al alloy exhibited the best mechanical performance. The study also indicated that the second phase strengthening and solid solution strengthening are the main mechanisms for the strengthening of the material, and the smaller c/a ratio may increase the ductility of the alloy.