Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Erfeng Han,Jie Gao,Rui Huang

DOI: https://doi.org/10.13251/j.issn.0254-6051.2017.05.016

2017-01-01

Abstract:Effects of solution temperature and aging time on microstructure and mechanical properties of Mg-7Gd-5Y alloy were studied,and its mechanism was analyzed.The results show that the as-cast alloy is mainly composed of α-Mg solid solution,Mg3(Gd,Y) phase,14H long period phase and RE-rich cubic phase.When solution temperature is 500 ℃,tensile strength of the alloy increases by 11% and the elongation increases by 2.4% compared with the original state,which show good strength and plastic combination.As the solution temperature increases,the grain boundary eutectic phase content of the alloy decreases gradually,long period phase becomes thin after solid solution at 500 ℃ for 10 h,and more stacking fault forms;as the aging time increases,the yield strength and tensile strength of the alloy first increase and then decrease,and get the maximum value when aging time is 120 h,meanwhile the elongation of Mg-7Gd-5Y alloy shows overall decreasing trend with the increase of aging time.