Microstructure and Mechanical Properties of As-Cast and Heat Treated Mg-15Gd-3Y Alloy

Zhang Lei,Dong Xuanpu,Li Jiqiang,Wang Wenjun,Wang Aihua,Fan Zitian

DOI: https://doi.org/10.1016/s1002-0721(10)60395-x

2011-01-01

Abstract:The microstructure evolution and mechanical properties of Mg-15Gd-3Y alloy were investigated in the as-cast and heat treated conditions. The microstructure evolution from as-cast to cast-T4 states involved a-Mg solid solution+Mg5(Gd,Y) phase→α-Mg supersaturated solid solution+rare earths compound Mg3(Gd1.26,Y0.74)→α-Mg supersaturated solid solution+rare earths compound Mg3(Gd0.745,Y1.255). It showed that 480 °C/4 h was the optimal solution treatment parameter. If the solution temperature was high or the holding time was long, such as 520 °C/16 h, an overheating phenomenon would be induced, which had a detrimental effect on the mechanical properties. When ageing at 225 and 200 °C, the alloy would exhibit a significant age-hardening response and great long-time-age-hardening potential, respectively. The best mechanical properties were obtained at the parameters of 480 °C/4 h+225 °C/16 h, with the UTS of 257.0 MPa and elongation of 3.8%.