Abstract:Inspections on microstructural design suggest that a high-strength Mg alloy can be achieved via the generation of co-precipitation of prismatic and basal precipitates with high number density and large aspect ratios. Currently, there is a lack of feasible approaches to generating such a microstructure. This work investigated the specific role of various Yb contents on the precipitation behavior, solute segregation and mechanical performance of cast Mg-9Gd-xYb-0.5Zn-0.2Zr alloys (x = 0, 0.5, 1 wt%). It was found that, the age hardening response of Mg-9Gd-0.5Zn-0.2Zr alloy could be significantly improved as the Yb addition increased, primarily ascribed to introduction of dense distribution of both prismatic and basal matrix precipitates involving gamma '', beta' and beta(1). Solute segregation of Yb had been examined utilizing high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), revealing the evidence of strong Yb segregation in both prismatic beta', beta(1) and basal gamma '' precipitates. Quantitative TEM analysis indicated that the increasing Yb addition was found to improve the number density of gamma '', beta' and beta(1) during isothermal ageing at 225 degrees C. The substantial improvement on yield strength (similar to 84 MPa) in peak-aged alloy was thereby achieved due to the co-precipitation of dense prismatic and basal strengthening phases associated with Yb addition (1 wt%). However, in addition to the promoted precipitation of these strengthening phases, Zn-Zr particles were confirmed to act as favorable nucleation sites for prismatic beta(1) phases in the under-aged condition. During prolonged ageing time, the addition of 1 wt% Yb was found to greatly accelerate the growth of these preferentially formed beta(1) phases and part of beta(1) transformed in situ into beta phases, accompanied by the gradual developments of matrix precipitate-free zones (PFZs). The greatly improved uneven distribution of these coarse beta-type phases concomitant with widened PFZs primarily led to the significant reduction in ductility as the Yb content increased up to 1%.

Effect of Y on Age Hardening Response and Mechanical Properties of Mg-xY–1.5LPC −0.4zr Alloys

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Age Hardening Characteristics and Mechanical Properties of Mg-3.5dy-4.0gd-3.1nd-0.4zr Alloy

Effects of Ageing Treatment on Microstructures and Properties of Mg–Gd–Y–Zr Alloys with and Without Zn Additions

Synergic Effects of Gd and Y Contents on the Age-Hardening Response and Elevated-Temperature Mechanical Properties of Extruded Mg–Gd(-Y)-Zn-Mn Alloys

The Role of Yb Content on the Microstructural Evolution and Mechanical Characteristics of Cast Mg-9Gd-0.5Zn-0.2Zr Alloy

Effects of Minor Y Addition on Microstructure and Mechanical Properties of Mg-Nd-Zn-Zr Alloy

Effect of Ageing Treatment on the Microstructure, Texture and Mechanical Properties of Extruded Mg–8.2Gd–3.8Y–1Zn–0.4Zr (wt%) Alloy

Effect of Misch Metal and Yttrium on the Ageing Behavior of AZ91 Magnesium Alloy

Effect of Gd Content on Microstructure and Mechanical Properties of Mg–Gd–Y–Zr Alloys under Peak-Aged Condition

Microstructure and High-Temperature Mechanical Properties of Mg-6Al Magnesium Alloy Containing Yttrium

Effect secondary deformation on microstructures and mechanical properties of Mg-6Gd-3.2Y-xZn-0.5Zr extruded sheet

Effects of heat treatment on mechanical properties of an extruded Mg-4.3Gd-3.2Y-1.2Zn-0.5Zr alloy and establishment of its Hall–Petch relation

Effects of Gadolinium on Aging Behavior and Mechanical Properties of Mg-5Y-3Nd-Zr Alloy

Effect of Ageing Treatment on the Precipitation Behaviour of Mg–Gd–Y–Zn–Zr Alloy

Effect of Yb Addition on the Microstructure and Mechanical Properties of the Mg–4Sm–3Gd–0.5Zr Alloy

Effect of aging on microstructure and hardness of Mg-5Y-3Sm-0.8Ca alloy

Effect of Zn Concentration on the Microstructures and Mechanical Properties of Extruded Mg–7Y–4Gd–0.4Zr Alloys

Ageing Behavior of Extruded Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt.%) Alloy Containing LPSO Phase and Γ′ Precipitates

A Preliminary Study on the Effects of Aging Temperature on the Microstructure and Mechanical Properties of As-Extruded Mg-12Gd-4Y-1Zn Magnesium Alloy