Abstract:Enhanced precipitation strengthening effect and ductility of Mg-9.8Gd-3.6Y-2.2Zn-0.4Zr alloy are achieved by short-time solution treatment prior to aging, and the effects of short-time solution on microstructure differences, strengthening contribution and fracture behavior are analyzed. The IF (initial-forged state) and PA (peak-aged state) samples exhibit the similar microstructure, with numerous fragmented lamellar LPSO phase distributed within the matrix and relatively uniform small grains (∼9μm). The significant increase in grain size of SS (solid solution state) and SSPA (solid solution + peak-aged state) samples (23.1μm and 27.0μm) is related to the lack of “pinning effect” caused by the dissolution of fragmented lamellar LPSO phase, meanwhile, the fully excited static recrystallization during the solution process results in high recrystallization fraction (above 95%) for both the two samples. The σgb (grain boundary strengthening) and σss (solid solution strengthening) contribute more than 70% in both IF and SS samples, while σgb and σpp (precipitation strengthening) dominate in the PA and SSPA samples. The stronger precipitation strengthening effect and age-hardening response of SSPA sample are derived from the more and denser β' precipitates within the matrix. The deformation mechanism of PA sample is the grain boundaries sliding of fine-sized grains and the slip of blocky LPSO phase, the microcracks are mainly concentrated at the grain boundaries, the blocky LPSO phase and its interface with matrix. As a comparison, the tensile deformation mechanism of SSPA sample is sufficient intragranular slip, the microcracks are mainly concentrated at the blocky LPSO phase and extend into the matrix, and finally forming large-sized cracks and deep fracture holes, which enhances the ductility. This paper may provide new ideas for the aging process design of wrought Mg-Gd-Y-Zn-Zr alloys.

Enhanced age-hardening response and mechanical properties of the Mg-Gd-Y-Zn-Zr alloy by trace Ag addition

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

On the role of Ag in enhanced age hardening kinetics of Mg–Gd–Ag–Zr alloys

A Comparative Study of the Role of Ag in Microstructures and Mechanical Properties of Mg-Gd and Mg-Y Alloys

Study on Solution and Aging Heat Treatment of a Super High Strength Cast Mg-7.8Gd-2.7Y-2.0Ag-0.4Zr Alloy

Synergic Effects of Gd and Y Contents on the Age-Hardening Response and Elevated-Temperature Mechanical Properties of Extruded Mg–Gd(-Y)-Zn-Mn Alloys

Enhanced Age-Hardening Response and Microstructure Study of an Ag-modified Mg–Sn–Zn Based Alloy

Improved age-hardening behavior of Mg-Sn-Mn alloy by addition of Ag and Zn

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effects of Gadolinium on Aging Behavior and Mechanical Properties of Mg-5Y-3Nd-Zr Alloy

Effect of Gd Content on Microstructure and Mechanical Properties of Mg–Gd–Y–Zr Alloys under Peak-Aged Condition

Effect of Y on Age Hardening Response and Mechanical Properties of Mg-xY–1.5LPC −0.4zr Alloys

Effects of Ageing Treatment on Microstructures and Properties of Mg–Gd–Y–Zr Alloys with and Without Zn Additions

Microstructure and Super High Strength of Cast Mg-8.5gd-2.3y-1.8ag-0.4zr Alloy

Enhanced Precipitation Strengthening Effect and Ductility of Mg-Gd-Y-Zn-Zr Alloy by Short-Time Solid Solution Prior to Aging

Microstructure and mechanical properties of cast Mg-6Gd–Zr alloy with different Y addition

Effect of Zn Concentration on the Microstructures and Mechanical Properties of Extruded Mg–7Y–4Gd–0.4Zr Alloys

Enhanced superplasticity in an extruded high strength Mg–Gd–Y–Zr alloy with Ag addition

Enhancing Strength and Creep Resistance of Mg–Gd–Y–Zn–Zr Alloy by Substituting Mn for Zr

Influences of Gd on the Microstructure and Strength of Mg–4.5Zn Alloy