Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Enhanced strength and corrosion resistant of Mg-Gd-Y-Al alloys by LPSO phases with different Al content

A Study on the Damping Capacities of Mg–Zn–Y-Based Alloys with Lamellar Long Period Stacking Ordered Phases by Preparation Process

Effect of Al element on microstructure, mechanical properties and damping capacity of LPSO-containing Mg-Y-Zn-Li alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructures and properties of as-cast rare Earth magnesium alloy with LPSO phase

Effect of the Morphology of Long-Period Stacking Ordered Phase on Mechanical Properties and Corrosion Behavior of Cast Mg-Zn-Y-Ti Alloy

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

Improving the corrosion resistance of Mg-8Li-3Al-2Zn alloy by combining Gd alloying and hot extrusion

Effect of Al addition on microstructure and mechanical properties of Mg−Gd−Zn alloys

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Effect of Substituting Y with Gd on LPSO Phase Dispersion and Mechanical Properties of Mg-2Ni-2Y Alloy

Crystal structure, phase content, and tensile properties of As-cast Mg–Gd–Y–Al alloys

CALPHAD-guided design of Mg-Y-Al alloy with improved strength and ductility via regulating the LPSO phase

The high cycle fatigue property of Mg-Gd-Y-Zn-Mn alloy enhanced by LPSO phase

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Roles of micro-alloyed Y and Gd in improving the corrosion resistance and mechanical properties of pure Mg

Improved Strength in Wrought Mg–Y–Ni Alloys by Adjusting the Block-Shaped LPSO Phase and Plate-Shaped Γ′ Phase

Microstructure and mechanical properties of as-cast Mg−8Li−xZn−yGd (x=1, 2, 3, 4; y=1, 2) alloys

Effect of Al Addition on Grain Refinement and Phase Transformation of the Mg-Gd-Y-Zn-Mn Alloy Containing LPSO Phase

Improving the corrosion resistance of MgZn1.2Gd Zr0.18 (x = 0, 0.8, 1.4, 2.0) alloys via Gd additions

Effects of Bulk LPSO Phases on Mechanical Properties and Fracture Behavior of As-Extruded Mg-Gd-Y-Zn-Zr Alloys