Abstract:Here, a new Mg-1Bi-1Mn-0.3Zn (BMZ110, wt%) wrought alloy designed by the dilute addition of Zn subjected to an appropriate extrusion processing that showed an excellent strength-ductility synergy at room temperature. The main results included four aspects as follows: 1) With dilute Zn addition, the as-cast BMZ110 alloy was refined into an approximately equiaxed-grained structure, since the solid solution of Zn provided a relatively high growth restriction factor. 2) The as-extruded BMZ110 alloy exhibited the finer average grain size and weaker basal texture intensity than the as-extruded BM11 alloy without Zn. The co-segregation of Bi and Zn solutes into grain boundaries was observed to impede grain growth during extrusion and further weaken texture intensity. Moreover, Zn atoms incorporated into Mg3Bi2 phases by replacing Bi atoms increasing the nucleation rate of Mg3Bi2 phases and refining their sizes. 3) Compared with the as-extruded BM11 alloy, the as-extruded BMZ110 alloy demonstrated the higher yield strength (~ 283.4 MPa), ultimate strength (~ 366.2 MPa) and elongation-to-failure (~ 26%). The size refinement of grains and second phases contributed to an extra strength increments. Grain boundary segregation enhanced grain boundary cohesion not only reducing the number density of grain boundary cracks, but also activating more slip modes and grain rotation for increasing the ductility. 4) The as-extruded BMZ110 alloy had the higher grain growth resistance than the as-extruded BM11 alloy during annealing. Solute segregation offered an effective obstacle to restrict grain boundary migration enlarging the activation energy (~ 112.2 kJ/mol) and further delaying the grain growth. Therefore, this work will be helpful for the development of new high performance low-alloyed Mg-Bi based wrought alloys to achieve extensive applications in industries.

Effect of a bimodal grain structure on corrosion behavior and tensile properties of low-alloyed Mg-1Bi-1Zn-1Ag alloy

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Exploiting an as-extruded fine-grained Mg-Bi-Mn alloy with strength-ductility synergy via dilute Zn addition

Design of Multicomponent Mg–Al–Zn–Sn–Bi Alloys with Refined Microstructure and Enhanced Tensile Properties

Tailoring bimodal grain structure of Mg-9Al-1Zn alloy for strength-ductility synergy: Co-regulating effect from coarse Al2Y and submicron Mg17Al12 particles

The Role of Bimodal-Grained Structure in Strengthening Tensile Strength and Decreasing Yield Asymmetry of Mg-Gd-Zn-Zr Alloys

Microstructure, Non-Basal Texture and Strength-Ductility of Extruded Mg-6Bi-3Zn Alloy

Effective strengthening and toughening in Zn–1Mg alloy with bimodal grain structure achieved by conventional extrusion

Role of bimodal-grained structure with random texture on mechanical and corrosion properties of a Mg-Zn-Nd alloy

Microstructure, Mechanical, and Corrosion Properties of Extruded Low-Alloyed Mg-xZn-0.2Ca Alloys

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

The Synergy Effect of Fine and Coarse Grains on Enhanced Ductility of Bimodal-Structured Mg Alloys

Effect of Bimodal Microstructure on the Tensile Properties and Fracture Toughness of Extruded Mg-9Gd-4Y-0.5Zr Alloy

A new strong and ductile multicomponent rare-earth free Mg-Bi-based alloy achieved by extrusion and subsequent short-term annealing

A bimodal grain structured Zn–0.5Ag–0.2Mg alloy with high strength and ductility achieved through combined ECAP and cold rolling

Effect of Grain Size and Volume Fraction of Eutectic Structure on Mechanical Properties and Corrosion Behavior of As-Cast Zn–Mg Binary Alloys

Elucidating the dependence of corrosion behavior and mechanical property on the grain structure of low-temperature as-extruded Mg–Zn–Ca–Zr alloy

Effect of composition on the microstructure and mechanical properties of Mg-Al-Zn alloys

Mechanistic Study of Mg-Mn-Al Extrusion Alloy with Superior Ductility and High Strength

Development of bimodal grain-structured Al-Zn-Mg-Cu-Zr alloys for strength-ductility synergy via microalloying with Hf and Sc

Effect of Zn/Mg ratio on the microstructure and properties of Al-xZn-2.0Mg-1.0Cu-0.2Zr-yTi ultrahigh-strength aluminum alloy extrusion