Abstract:Here, a new Mg-1Bi-1Mn-0.3Zn (BMZ110, wt%) wrought alloy designed by the dilute addition of Zn subjected to an appropriate extrusion processing that showed an excellent strength-ductility synergy at room temperature. The main results included four aspects as follows: 1) With dilute Zn addition, the as-cast BMZ110 alloy was refined into an approximately equiaxed-grained structure, since the solid solution of Zn provided a relatively high growth restriction factor. 2) The as-extruded BMZ110 alloy exhibited the finer average grain size and weaker basal texture intensity than the as-extruded BM11 alloy without Zn. The co-segregation of Bi and Zn solutes into grain boundaries was observed to impede grain growth during extrusion and further weaken texture intensity. Moreover, Zn atoms incorporated into Mg3Bi2 phases by replacing Bi atoms increasing the nucleation rate of Mg3Bi2 phases and refining their sizes. 3) Compared with the as-extruded BM11 alloy, the as-extruded BMZ110 alloy demonstrated the higher yield strength (~ 283.4 MPa), ultimate strength (~ 366.2 MPa) and elongation-to-failure (~ 26%). The size refinement of grains and second phases contributed to an extra strength increments. Grain boundary segregation enhanced grain boundary cohesion not only reducing the number density of grain boundary cracks, but also activating more slip modes and grain rotation for increasing the ductility. 4) The as-extruded BMZ110 alloy had the higher grain growth resistance than the as-extruded BM11 alloy during annealing. Solute segregation offered an effective obstacle to restrict grain boundary migration enlarging the activation energy (~ 112.2 kJ/mol) and further delaying the grain growth. Therefore, this work will be helpful for the development of new high performance low-alloyed Mg-Bi based wrought alloys to achieve extensive applications in industries.

Low-temperature high-speed extrusion of a multicomponent Mg–Bi base alloy and its heat resistance during hot tension

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Achieving high strength near 400 MPa in an ultra-fine grained Mg–Bi–Ca ternary alloy via low-temperature extrusion

Microstructure, Non-Basal Texture and Strength-Ductility of Extruded Mg-6Bi-3Zn Alloy

Novel Mg-Bi-Mn wrought alloys: The effects of extrusion temperature and Mn addition on their microstructures and mechanical properties

Microstructure evolution, strengthening mechanisms and deformation behavior of high-ductility Mg−3Zn−1Y−1Mn alloy at different extrusion temperatures

Exploiting an as-extruded fine-grained Mg-Bi-Mn alloy with strength-ductility synergy via dilute Zn addition

Effect of Bi Addition on the Heat Resistance of As-Extruded AZ31 Magnesium Alloy

Achieving superior mechanical properties in a low-alloyed magnesium alloy via low-temperature extrusion

Development of ultrahigh-strength low-alloy Mg-0.7Al-0.3Ca-0.4Mn (wt.%) alloy with excellent ductility via controlling extrusion temperature

Achieving exceptional ultrahigh-strength in low-alloy Mg-1Al-1Ca-0.4Mn (wt%) alloy by regulating bimodal microstructure

Microstructures and Mechanical Properties of Extruded Mg-9Gd-4Y-0.6Zr-T5 at Elevated Temperatures

Developing a high-speed-extruded BMZQ5100 alloy with higher strength and microstructural thermal stability than AZ91 alloy

Microstructure and tensile properties of a low-alloyed magnesium alloy: effect of extrusion temperature

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Deformation behaviors and the related high-temperature mechanical properties of Mg-11Gd-5Y-2Zn-0.7Zr via regulating extrusion temperatures

Enhanced Mechanical Properties in Fine-Grained Mg–1.0Zn–0.5Ca Alloys Prepared by Extrusion at Different Temperatures

Effect of Hot Extrusion on Microstructure, Texture, and Mechanical Properties of Mg-Zn-Mn-0.5Ca Alloy

A high-performance Mg-Al-Sn-Zn-Bi alloy fabricated by combining sub-rapid solidification and hot rolling

Microstructure and Mechanical Properties of Moderate-Speed Extrudable Mg-Gd-Sm-Zr Alloy

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion