Abstract:A low-alloyed Mg-1.2Zn-0.1Ca (wt.%) alloy was fabricated via low-temperature extrusion and annealing at 250 & DEG;C for different times (10, 30, and 90 min) to attain heterostructures with different fine-grained fractions, focusing on the effect of heterostructure on the mechanical properties. Partial dynamic recrys-tallization (RX) occurred during extrusion at 150 & DEG;C, and a lamellar structure consisting of fine RX grains and coarse unRX grains was obtained. The subsequent annealing promoted static RX in the as-extruded alloy, leading to an increased fine-grained fraction from 67% to 95%. Meanwhile, the co-segregation of Zn and Ca atoms impeded the migration of grain boundaries, thus achieving a fine grain size of 0.8- 1.6 & mu;m. The sample annealed for 10 min with a fine-grained fraction of 73% and an average RX grain size of 0.9 & mu;m exhibited a superior combination of high yield strength (305 MPa) and good ductility (20%). In comparison, an excellent elongation of 30% was achieved in the alloy with a nearly fully-RXed mi-crostructure and an average grain size of 1.6 & mu;m after 90 min annealing, despite a lower yield strength of 228 MPa. In unRX grains, the hard orientation with ( 01-10 ) parallel to the extrusion direction and high-density dislocations made it more difficult to deform compared with the RX grains, thus producing hetero-deformation induced (HDI) strengthening. Besides fine grains and high-density dislocations, HDI strengthening is the key to achieving the superior mechanical properties of the low-alloyed Mg alloy. & COPY; 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Achieving superior mechanical properties in a low-alloyed magnesium alloy via low-temperature extrusion

Achieving High-Strength in Mg-0.8Zn-0.2Zr (wt.%) Alloy Extruded at Low Temperature

Development of High-Performance Mg–Zn–Ca–Mn Alloy Via an Extrusion Process at Relatively Low Temperature

Microstructure and tensile properties of a low-alloyed magnesium alloy: effect of extrusion temperature

Enhanced Mechanical Properties in Fine-Grained Mg–1.0Zn–0.5Ca Alloys Prepared by Extrusion at Different Temperatures

Achieving Superior Strength-Ductility Synergy in a Heterostructured Magnesium Alloy Via Low-Temperature Extrusion and Low-Temperature Annealing

Effect of Extrusion Temperatures on Microstructures and Mechanical Properties of Mg-3Zn-0.2Ca-0.5Y Alloy

Origins of High Ductility Exhibited by an Extruded Magnesium Alloy Mg-1.8Zn-0.2Ca: Experiments and Crystal Plasticity Modeling

Effect of Initial Microstructure Prior to Extrusion on the Microstructure and Mechanical Properties of Extruded AZ80 Alloy with a Low Temperature and a Low Ratio

A High-Ductility Mg–Zn–Ca Magnesium Alloy

On Mechanical Properties and Superplasticity of Mg–15Al–1Zn Alloys Processed by Reciprocating Extrusion

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Fabrication of high strength-ductility Mg-3.8Al-1.1Sn-0.4Ca alloy via differential-thermal asymmetric extrusion

Achieving Low-Temperature Superplasticity of a Coarse-Grained BAZ531 Magnesium Alloy

Microstructure, Texture and Mechanical Properties of Mg-3.0Zn-0.2Ca Alloys Fabricated by Extrusion at Various Temperatures

Manufacturing High-Performance Mg Alloy Through Hot Extrusion

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

High Strength and Superior Ductility of an Ultra-Fine Grained Magnesium–manganese Alloy

Mechanical properties of Mg-Ce-Y-Zr-Zn-Ca microalloyed magnesium alloys composed of near-atomic solute

Evolution of Microstructure and Mechanical Properties of Mg–3.0Zn–0.2Ca–0.5Y Alloy by Extrusion at Various Temperatures

Effect of Hot Extrusion on Microstructure, Texture, and Mechanical Properties of Mg-Zn-Mn-0.5Ca Alloy