Abstract:The microstructure evolution and thermal stability of continuous SiC fiber-reinforced Ti60 (SiCf/Ti60) composites at elevated temperatures have not been reported. The objective of this study was to conduct thermal exposure experiments of SiCf/Ti60 composites at 400 degrees C / 100 h, 600 degrees C / 100 h, and 800 degrees C / 100 h. The aim was to compare the interfacial and matrix microstructures under hot isostatic pressure (HIP) conditions and to assess their thermal stability. The results show that SiCf/Ti60 composites have excellent long-term thermal stability at 600 degrees C thermal exposure, short-term thermal stability at 800 degrees C thermal exposure and the thickness of the reaction layer (RL) increases to 1.27 mu m. From HIP to 800 degrees C thermal exposure, RL changes from finegrained TiC II discontinuous silicides II coarse-grained TiC to fine-grained TiC II near-continuous silicides II medium-grained TiC II coarse-grained TiC. Large-sized beta-Ti and S2 silicides precipitated in the matrix at 800 degrees C thermal exposure, where beta-Ti and alpha-Ti followed the Burgers orientation relationship (BOR), and the S2 exhibited a multitude of orientation relationships with both beta-Ti and alpha-Ti. Furthermore, it was demonstrated that thermal exposure resulted in a reduction in the dislocation density of the matrix. In particular, thermal exposure at 800 degrees C led to a decrease in the dislocation density of the matrix by 47 %. This observation provided a novel approach for the reduction of crystal defects in the matrix and the enhancement of the properties of SiCf/Ti composites.

Microstructural Evolution and Phase Transformation of Cansas 3303 SiC Fibers During Thermal Shock at 1200°C

Structural evolution and mechanical properties of Cansas-III SiC fibers after thermal treatment up to 1700 °C

Mechanical properties and microstructural evolution of Cansas-III SiC fibers after thermal exposure in different atmospheres

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

The fiber structure evolution and performance changes of SiC–ZrC fibers after 1600 °C heat treatment

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Thermal stability of CVI and RMI SiC/SiC composites adopting Cansas 3303 SiC fibers

Failure Evaluation of a SiC/SiC Ceramic Matrix Composite During In-Situ Loading Using Micro X-ray Computed Tomography

Effect of long-time annealing at high temperature on the microstructure and mechanical properties of different types of SiC fibers

High-temperature tensile behavior of 3D SiC/SiC composites

Multiscale Failure Mechanism Analysis of SiC Fiber-Reinforced TC17 Composite Subjected to Transverse Tensile Loading at Elevated Temperature

Finite Element Simulation of Stress Distribution and Development of C-F/Sic Ceramic-Matrix Composite Coated with Single Layer Sic Coating During Thermal Shock

In-situ Tensile Damage and Fracture Behavior of PIP SiC/SiC Minicomposites at Room Temperature

Effect of heat treatment on the microstructure and properties of CVD SiC fiber

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

Influence of Thermal Shock on the Mechanical Behavior of Si-SiC Coated Carbon/Carbon Composites

Microstructure and corrosion behavior of in-situ grown Y3Si2C2 coated SiC fibers exposed to air and wet-oxygen at 1400 °C

High-temperature Microstructure Evolution and Thermal Stability of SiCf/Ti60 Composites

Microstructural and mechanical evolution of SiCf/SiC composites in wet oxygen atmosphere above 1000 degrees C