Abstract:Transverse mechanical properties of titanium matrix composites (TMCs) play an important role during its engineering service. Although SiCf / TC17 composite is one of the most promising TMC candidates for aeroengine, as we know its transverse properties have not been reported yet until now. In this work, the transverse strength of single SiC fiber reinforced TC17 composite was evaluated using cruciform specimen. The surface and cross-section of fractured specimen were investigated by SEM to determine the failure position during tensile test. Finite element simulation method was also used to analyze the mechanism of interfacial failure and crack propagation. During the transverse tensile test of single fiber specimen, the initial non-linearity in the stress-strain curve occurred at the stress of (271 +/- 12) MPa, which indicated the beginning of fiber-matrix interface failure. SEM observation showed that the crack in the center of sample appeared at the interface of reaction layer and carbon coating with a 24 degrees similar to 68 degrees angle to the applied loading direction and its length extended with the increase of the applied stress. The finite element simulation results based on bilinear cohesive element model showed that transverse fracture of composite interface was shear failure mode, which agreed well with the test results. Before the occurrence of non-linearity in the stress-strain curve, the crack initiated at the circular interface between reaction layer and carbon coating with a 40 degrees similar to 50 degrees angle to the applied loading direction. Crack initiation locations in test samples were different with those in simulation samples, because the actual composite interface was rough and some micro-flaws formed in the interface, whereas it was assumed to be an ideal rigid interface for simulation. Then the crack propagated along both circumferential and axial directions because of the shear stress. With the crack growing, the interface close to 0 degrees angle to the applied loading direction failed first caused by the radial tensile stress, whereas the interface near 90 degrees failed later as a result of circumferential shear stress. After complete failure of the interface, stress redistribution occurred around the SiC fiber and the interface separation increased with the increasing of the applied load, which gave rise to the yielding and deforming of the matrix near fiber until the final fracture of the composite.

Multiscale Failure Mechanism Analysis of SiC Fiber-Reinforced TC17 Composite Subjected to Transverse Tensile Loading at Elevated Temperature

Research on Single SiC Fiber Reinforced TC17 CompositesUnder Transverse Tension

FEM Analysis of the Stress Response and Failure Mechanism of SiC-coated Cf/ SiC Composites During Thermal Shock

Study on Tensile Behavior of Sicf/Tc17 Composites

Analysis of Multi-scale Failure Behavior of SiC f /SiC Composite Clad Tube under Flexible Clamping Damage

An Efficient Multi-Scale Method for Failure Mechanism Analysis of SiCf/Ti Composites with Experimental Validation

Numerical simulation of the interface failure mechanism of SiC/Ti-6Al-4V composites under the transverse tensile stress

Failure Mechanism of Continuous Fiber-Reinforced Titanium Matrix Composite Bling under Rotational Loading

Multi-scale Progressive Damage and Failure Behavior Analysis of Three-Dimensional Winding SiC Fiber-Reinforced SiC Matrix Composite Tube

Damage accumulation during high temperature fatigue of Ti/SiC$_f$ metal matrix composites under different stress amplitudes

Multiscale investigation on fatigue properties and damage of a 3D braided SiC/SiC plus PyC/SiC composites in the full stress range at 1300 C

Internal Damage Evolution Investigation of C/SiC Composites Using In-Situ Tensile X-ray Computed Tomography Testing and Digital Volume Correlation at 1000 °C

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Low-cycle Fatigue Behavior and Damage Progression of a Fiber Reinforced Titanium Matrix Composite

Damage accumulation during high temperature fatigue of Ti/SiCf metal matrix composites under different stress amplitudes

Fatigue Behaviors of C/Mo Double-Coated SiC Fiber-Reinforced Ti6Al4V Composites with Varied Interfacial Microstructure

An Overview of Tensile and Shear Failure Mechanisms of Silicon Carbide-Based Ceramic Matrix Composites

Cyclic Deformation and Low Cycle Fatigue Behavior in a SiCw/6061Al Composite at Elevated Temperature

Tensile Behavior of 2D-C/sic Composites at Elevated Temperatures: Experiment and Modeling

Simulation of Damage and Failure Processes of Interpenetrating SiC/Al Composites Subjected to Dynamic Compressive Loading