Abstract:SiC/SiC composites in aerospace applications are exposed to a variety of thermal conditions, in particular, thermal stress due to rapid heating and cooling. Therefore, it is crucial to investigate and evaluate the resistance of SiC/SiC composites to repeated temperature cycling. This paper investigates the evolution of properties and damage mechanisms of 2D and 2.5D SiC/SiC composites after different thermal shock cycles at 1300 °C. It was found that SiC/SiC composites exhibit a temporary weight increase at the beginning of the thermal shock cycle. Subsequently, the weight decreases and stabilizes as the number of thermal shocks increases. After 10–30 thermal shocks at 1300 °C, the density of SiC/SiC composites decreases while the porosity increases. The fracture behavior of SiC/SiC composites remains the same as that of the initial composites, with 2D SiC/SiC composites exhibiting pseudo-tough fracture and 2.5D SiC/SiC composites exhibiting brittle fracture. The residual strength of the SiC/SiC composites decreased slightly while the residual modulus remained stable. This is related to the reaction of the SiC, and BN with water and oxygen at high-temperature. The thermal shock damage of SiC/SiC composites is anisotropic and is influenced by the structure of the fiber preforms. This is due to the difference in thermal expansion coefficients of the components within the composites and the structural properties of the fiber preforms.

Thermal stability of CVI and RMI SiC/SiC composites adopting Cansas 3303 SiC fibers

Structural evolution and mechanical properties of Cansas-III SiC fibers after thermal treatment up to 1700 °C

Residual stress variation in SiCf/SiC composite during heat treatment and its effects on mechanical behavior

High-temperature tensile behavior of 3D SiC/SiC composites

The fiber structure evolution and performance changes of SiC–ZrC fibers after 1600 °C heat treatment

Thermal Expansion Behavior of Carbon Fiber Reinforced Chemical-Vapor-infiltrated Silicon Carbide Composites from Room Temperature to 1400 °C

Effect of long-time annealing at high temperature on the microstructure and mechanical properties of different types of SiC fibers

The effect of deposition temperature of BN interphase on the tensile properties of SiC fibers

High temperature bending properties and failure mechanism of 3D needled C/SiC composites up to 2000 °C

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

Effect of CVI SiC interphase on tensile properties of SiC fibers with different surfaces

Influence of High-Temperature Oxidation and Test Conditions on the Dynamic Mechanical Properties of 2.5D SiCf/SiCm Composites

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Effects of interfacial residual stress on mechanical behavior of SiCf/SiC composites

Effects of Interphase Thickness and Heat Treatment on Transverse Thermal Diffusivity of 3 D C / SiC Composites

EFFECTS OF HEAT TREATMENT ON THERMAL EXPANSION OF 3D C/SiC COMPOSITES

Study of SiC fiber axial compressive behavior using tensile recoil measurement

Microstructure evolution and thermal conductivity of diamond/SiC composites after heat treatment

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

Effect of thermal residual stress on the tensile properties and damage process of C/SiC composites at high temperatures