Abstract:This article investigates the evolution of surface transverse cracks in Q345 steel during the hot‐rolling process. A slab rolling model is established based on the onsite rolling process parameters to analyze the effects of different rolling processes on the morphology and aspect ratio of surface cracks. The study summarizes the evolutionary behavior of surface transverse cracks under various rolling process parameters. This article examines the evolutionary behavior of transverse surface cracks in Q345 steel during the hot‐rolling process under various rolling conditions. "V"‐shaped cracks are prefabricated on the billet surface for laboratory hot‐rolling tests, and a corresponding rolling model is developed to validate its accuracy. The slab rolling model is established based on actual onsite rolling process parameters. The aim is to analyze the effects of different rolling conditions on the surface crack morphology and aspect ratio. The results indicate that variations in roll diameter (1400, 1300, and 1200 mm) influence crack propagation, with cracks unfolding earlier when the roll diameter is 1400 mm. At varying initial rolling temperatures (1300, 1200, and 1100 °C), cracks begin to unfold earlier at the highest temperature of 1300 °C. When examining different friction coefficients (0.4, 0.5, and 0.6), cracks unfold earlier at the highest coefficient of 0.6. Similarly, at different rolling speeds (3, 4, and 5 m s−1), cracks unfolded earlier at the highest speed of 5 m s−1. Analysis of changes in crack depth and aspect ratio during rolling shows that the initial few passes have a greater influence on crack depth and unfolding. In the later stages of rolling, cracks continue to unfold, though the depth shows minimal variation, and the aspect ratio tends to approach zero.

The Cracks on Slab Corner During Hot Rolling Process

Behavior of Transversal Crack on Slab Corner During V-H Rolling Process

Research on the Behavior of Transversal Crack in Slab V–H Rolling Process by FEM

Behaviour of longitudinal cracks on slab surfaces in V-H rolling processes

Research on Behavior of Slab Surface Defects in Forward Slip Zone during V-H Rolling Process

Analysis of Crack Tip Stress of Transversal Crack on Slab Corner During Vertical-Horizontal Rolling Process by FEM

Thermal-Mechanical Finite Element Analysis of Evolution of Surface Cracks During Slab Rolling

The Causes and Control of Longitudinal Edge Cracks of the Plate

Evolution of Surface Crack on Slab During Rough Rolling Using Thermal-Mechanical FEM

Effect of Rolling Process Parameters on Transverse Cracks on the Surface of Q345 Steel

Investigation of Closure of Internal Cracks During Rolling by FE Model Considering Crack Surface Roughness

Research on Crack Healing in Slab During Hot Rolling

Friction and Slab Deformation Behaviour During Rough Rolling

Continuous Simulation of Slab Deformation During Multi-Pass Rolling.

Review on Factors of Surface Cracks in Slab and Their Behavior During Rolling

Closure Behavior of Spherical Void in Slab During Hot Rolling Process

Evolution of subsurface blisters and initiation of surface crack on slab during hot rolling using FEM

INFLUENCES OF EDGING ROLL SHAPE ON THE PLASTIC STRAIN DISTRIBUTION OF SLAB DURING MULTI-PASS V-H ROLLING PROCESS

Causes of Transverse Corner Cracks in Microalloyed Steel in Vertical Bending Continuous Slab Casters

Numerical Simulation and Experimental of Forming Defects in Roll-Bending Process for Z-Shaped Profiles With Large Cross-Section

Formation Mechanism of Edge Crack During Hot Rolling Process of High-Grade Non-Oriented Electrical Steel