Abstract:This study investigated defect formation and strain distribution in high-Mg-content Al-Mg alloys during normal rolling and cross-rolling processes. The finite element analysis (FEA) revealed the presence of wave defects and strain localization-induced zipper cracks in normal cold rolling, which were confirmed by the experimental results. The concentration of shear strain played a significant role in crack formation and propagation. However, the influence of wave defects was minimal in the cross-rolling process, which exhibited a relatively uniform strain distribution. Nonetheless, strain concentration at the edge and center regions led to the formation of zipper cracks and edge cracks, with more pronounced propagation observed in the experiments compared to FEA predictions. Furthermore, texture evolution was found to be a crucial factor affecting crack propagation, particularly with the development of the Goss texture component, which was observed via electron backscattered diffraction analysis at bending points. The Goss texture hindered crack propagation, while the Brass texture allowed cracks to pass through. This phenomenon was consistent with both FEA and experimental observations. To mitigate edge crack formation and propagation, potential strategies involve promoting the formation of the Goss texture at the edge through alloy and process conditions, as well as implementing intermediate annealing to alleviate stress accumulation. These measures can enhance the overall quality and reliability of Al-Mg alloys during cross-rolling processes. In summary, understanding the mechanisms of defect formation and strain distribution in Al-Mg alloys during rolling processes is crucial for optimizing their mechanical properties. The findings of this study provide insights into the challenges associated with wave defects, strain localization, and crack propagation. Future research and optimization efforts should focus on implementing strategies to minimize defects and improve the overall quality of Al-Mg alloys in industrial applications.

Micro Crack of Aluminum Sheet During Cold Rolling

Surface Oxide Fracture in Cold Aluminium Rolling

Edge crack forming mechanism and the countermeasures in as‐sintered 2024 aluminium alloy during cold rolling

Tensile Fracture of Ultrafine Grained Aluminum 6061 Sheets by Asymmetric Cryorolling for Microforming

Study on Rolling Defects of Al-Mg Alloys with High Mg Content in Normal Rolling and Cross-Rolling Processes

Uncommon Cold-Rolling Faults in an Fe–Mn–Si–Cr Shape-Memory Alloy

Microstructures and textures in cold-rolled aluminium strip

Comparison of edge crack behavior of Mg sheets prepared by online heating rolling

Effects of operation parameters of cold rolling on surface finish of aluminum

Crystal Plasticity Finite Element Simulation of Grain Evolution Behavior in Aluminum Alloy Rolling

Effects of intermediate annealing and rolling on plastic failure and grain refinement of Al-Mg-Li alloy

Microstructural Evolution and Mechanical Behavior of Pure Aluminum Ultra-Thin Strip under Roller Vibration

Micro-crack Tip Fracture of Commercial Grade Aluminum under Mixed Mode Loading

Initiation and Suppression of Crack Propagation during Magnesium Alloy Rolling

Influence of Asymmetric Rolling on the Microstructure, Texture Evolution and Mechanical Properties of Al–Mg–Si Alloy

Evolution of Surface Crack on Slab During Rough Rolling Using Thermal-Mechanical FEM

Effect of Rolling Process Parameters on Transverse Cracks on the Surface of Q345 Steel

Microstructural Evolution and Mechanical Properties of Pure Aluminum upon Multi-Pass Caliber Rolling

Analysis on peeling defects of cold-rolled sheet and its influencing factor

Mechanical property enhancement and microstructure evolution of an Al-Cu-Li alloy via rolling at different temperatures

The Cracks on Slab Corner During Hot Rolling Process